Abstract:For CO2 methanation reaction, a Mg species is often utilized as the alkaline promotor for Ni based catalysts to enhance the low-temperature catalytic activity. Herein, based on a pioneer ordered mesoporous NiO-Al2O3 catalyst, a Mg alkaline promotor had been incorporated into the ordered mesoporous framework via a one-pot evaporation induced self-assembly (EISA) strategy. As a result, the ordered mesoporous NiO-MgO-Al2O3 composite oxides with Mg/Al molar ratios in a wide range (0-10%) were successfully fabricated and directly utilized as the catalysts for CO2 methanation reaction. These mesoporous catalysts were carefully characterized by X-ray diffraction, N-2 adsorption-desorption, transmission electron microscopy, selected area electron diffraction, energy dispersive spectrometer, X-ray photoelectron spectroscopy, H-2 temperature-programmed reduction, and CO2 temperature-programmed desorption measurements. It was found that the ordered mesoporous materials with large specific surface areas (180.8-232.8 m(2) g(-1)), big pore volumes (0.37-0.43 cm(3) g(-1)), and narrow pore size distributions (around 9.5 nm) could be successfully retained after the calcination at 700 degrees C. The highly dispersed Ni species were strongly interacted with the mesoporous framework in the form of NiAl2O4 spinel. The incorporation of the Mg progressively increased the surface basicity of these catalysts, which could intensify the chemisorption and activation of CO2 during the CO2 methanation reaction. Therefore, the low-temperature catalytic activity was significantly enhanced. The "volcano-shape curve" relationship between the Mg/Al molar ratio and catalytic activity had been interestingly observed, suggesting only appropriate surface basicity could obtain the optimum catalytic activity. Besides, there was no evident deactivation over these mesoporous catalysts after 50 h long-term stability tests due to the confinement effect of the mesoporous framework. Therefore, the present ordered mesoporous NiO-MgO-Al2O3 materials could be considered as a series of potential catalyst candidates for CO2 methanation.

One-Pot Synthesis of Ordered Mesoporous NiSiAl Oxides for Catalyzing CO2 Reforming of CH4

One-Pot Synthesis of Ordered Mesoporous NiO–CaO–Al2O3Composite Oxides for Catalyzing CO2Reforming of CH4

Significant roles of mesostructure and basic modifier for ordered mesoporous Ni/CaO–Al2O3 catalyst towards CO2 reforming of CH4

Ordered Mesoporous Alumina Supported Nickel Based Catalysts for Carbon Dioxide Reforming of Methane

Ordered Mesoporous MgO–Al2O3 Composite Oxides Supported Ni Based Catalysts for CO2 Reforming of CH4: Effects of Basic Modifier and Mesopore Structure

One‐pot Synthesis of Ordered Mesoporous NiCeAl Oxide Catalysts and a Study of Their Performance in Methane Dry Reforming

Carbon Dioxide Reforming of Methane over Ordered Mesoporous NiO–MgO–Al2O3 Composite Oxides

Carbon Dioxide Reforming of Methane over Cobalt‐Nickel Bimetal‐Doped Ordered Mesoporous Alumina Catalysts with Advanced Catalytic Performances

One-step synthesis of ordered mesoporous CoAl2O4 spinel-based metal oxides for CO2 reforming of CH4

Facile Route for Synthesizing Ordered Mesoporous Ni–Ce–Al Oxide Materials and Their Catalytic Performance for Methane Dry Reforming to Hydrogen and Syngas

Synthesis of nickel catalysts supported on Zr-doped ordered mesoporous Al2O3 and their catalytic performance for low-temperature CO2 reforming of CH4

Alkaline-promoted Co-Ni Bimetal Ordered Mesoporous Catalysts with Enhanced Coke-Resistant Performance Toward CO 2 Reforming of CH 4

Ni-based Catalyst Supported on Ordered Mesoporous Al2O3 for Dry CH4 Reforming: Effect of the Pore Structure

CO2 Reforming of CH4 over Rare Earth Elements Functionalized Mesoporous Ni–Ln (ln = Ce, La, Sm, Pr)–Al–O Composite Oxides

MoOx-Doped Ordered Mesoporous Ni/Al2O3 Catalyst for CO Methanation

Organic Additive Assisted Ordered Mesoporous Ni/Al2O3 Catalyst for CO2 Methanation

Alkaline-promoted Ni based ordered mesoporous catalysts with enhanced low-temperature catalytic activity toward CO2 methanation

CO2 methanation over ordered mesoporous NiRu-doped CaO-Al2O3 nanocomposites with enhanced catalytic performance

One-Pot Synthesis of Hexagonal Mesoporous Silica Confined Ni Based Catalysts with Advanced Co2 Methanation Performance

Meso-porous Ni/Mg/Al catalysts for methane reforming with CO2

Ordered mesoporous Ni–Mg–Al2O3 as an effective catalyst for CO2 reforming of CH4