Electrocatalytic Performances of Phosphorus Doped Carbon Supported Pd Towards Formic Acid Oxidation

Jianding Li,Qifeng Tian,Shiyue Jiang,Yao Zhang,Yuanxin Wu

DOI: https://doi.org/10.1016/j.electacta.2016.06.041

IF: 6.6

2016-01-01

Electrochimica Acta

Abstract:A new kind of phosphorus contained carbon support (PC) was fabricated by calcining the mixture of the carbon and triphenylphosphine under nitrogen. The Pd/P-C and Pd/C catalysts were synthesized by liquid reduction method. The catalysts were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). Well-dispersed Pd nanoparticles were obtained and their particle sizes are in the range of 3.5–4.5nm. Electrochemical measurements demonstrated that when the mixture of carbon and triphenylphosphine were annealed at 800°C, the activity of the corresponding catalyst (Pd/P-C-800) was enhanced as a factor of 3.14 than the Pd/C catalyst. A negative shift (76mV than Pd/C) of CO stripping peak and improved stability were observed for the Pd/P-C-800 catalyst. Moreover, faster charge-transfer kinetics of the formic acid oxidation for the Pd/P-C-800 catalyst was determined through electrochemical impedance spectroscopy (EIS) measurements. The better catalytic activity and stability of the Pd/P-C catalyst are ascribed to the doping of phosphorus in the carbon support.