Abstract:Activated carbon support Pd nanoparticles (NPs) modified by various WO₃-shaped catalysts were prepared and applied as an efficient anode catalyst for direct formic acid fuel cells. Three forms of WO₃ (nanosheets, nanoparticles, nanobars) modified activated carbon hybrids were first prepared via different syntheses, and then used as supports to synthesize three types of Pd-WO₃/C catalysts by a NaBH4 reduction method. The morphology, structure, and electrochemical performances of the as-prepared Pd-WO₃/C catalysts were characterized and analyzed. We can see that the noble metal particles loaded with activated carbon modified by WO₃ exhibit small particle size and uniform dispersion from the transmission electron microscope image. The synthesized composite catalysts was used for the formic acid electrooxidation and showed excellent catalytic performance. The oxidation peak current density of the Pd/WO₃-Nanosheets/C (40.04 mA·cm-2 was the highest, approximately 1.2 times that of Pd/C (33.00 mA·cm-2. Additionally, the long-term stability (i-t) test results show that the Pd/WO₃-Nanosheets/C catalyst exhibits superior stability during formic acid electrooxidation. The reason for the increase in performance can be attributed to the following: the large specific surface area of WO₃ decreases the adsorption strength of intermediates such as COad on Pd and prevents the accumulation of poisonous intermediates, thereby promoting the oxidation reaction of formic acid in the direct pathway; the catalyst-support interaction between precious metal Pd and WO₃, substantially improving the catalytic performance of Pd-WO₃/C catalysts.

Effect of carbon modification on electrocatalytic performance of carbon supported Pd catalysts

Effect of Nitric Acid Pretreatment on the Properties of Activated Carbon and Supported Palladium Catalysts

Enhanced Electro-Oxidation of Formic Acid by a PdPt Bimetallic Catalyst on a CeO_2-modified Carbon Support

Influence of Preparation Condition on the PdHx Phase of Pd/C Catalyst

Nitrogen-doped Carbon-Modified Titanium Oxides Supported Pd Catalyst for the Electrooxidation of Formic Acid

An Effective Pd@Ni-B/C Anode Catalyst for Electro-Oxidation of Formic Acid

Electrocatalytic Performances of Phosphorus Doped Carbon Supported Pd Towards Formic Acid Oxidation

Electro-catalysis of carbon black or titanium sub-oxide supported Pd–Gd towards formic acid electro-oxidation

Carbon-supported Pd catalysts: Influences of nanostructure on their catalytic performances for borohydride electrochemical oxidation

The Effect of Carbon Support Treatment on the Stability of Pt/C Electrocatalysts

Effect of Nabh4 Concentration and Synthesis Temperature on the Performance of Pd/C Catalyst for Formic Acid Electro-Oxidation

Pd Nanoparticles Supported on Carbon-Modified Rutile TiO2 As a Highly Efficient Catalyst for Formic Acid Electrooxidation

Effect of Pretreatment Method of Activated Carbon on the Adsorption of NO over Supported Pd Catalyst

Controllable Synthesis of Carbon Nanofiber Supported Pd Catalyst for Formic Acid Electrooxidation

Preparation and Characterizations of Highly Dispersed Carbon Supported PdxPty/C Catalysts by a Modified Citrate Reduction Method for Formic Acid Electrooxidation

Carbon-Supported Pd−Pt Nanoalloy with Low Pt Content and Superior Catalysis for Formic Acid Electro-oxidation

Electrocatalytic Oxidation of Formic Acid on the Carbon Supported Pd-Ni Alloy Nanoparticles

Effect Of Pretreatment Of Carbon Supports On Activity Of Cotmpp Electrocatalysts For The Reduction Of Oxygen

Mixed Heteropolyacids Modified Carbon Supported Pd Catalyst For Formic Acid Oxidation

Various Morphology of WO3 Modified Activated Carbon Supported Pd Catalysts with Enhanced Formic Acid Electrooxidation

Effect of Thermal Treatment of Pd Decorated Fe/C Nanocatalysts on Their Catalytic Performance for Formic Acid Oxidation.