Abstract:Magnesium alloys are potentially attractive biodegradable materials. However, their rapid corrosion rate limits their biomedical application. To slow down the rate of biodegradation, a protective calcium-phosphate coating was formed on a magnesium alloy substrate by a hydrothermal method. Scanning electron microscope results showed that the coating consisted of two layers with different crystalline characteristics. The loose outer layer showed a prism-like crystal structure, while the compact inner layer is a dense ultra-fine regular di-pyramid-like structure with an average grain dimension of ∼200 nm. The compositions of the inner layer and outer layer were calcium-deficient hydroxyapatite (Ca-def HA) and dicalcium phosphate (DCPa), respectively. The coating adhered well to the substrate with a thickness of about 15 μm. Immersion in Hank’s solution indicated that the coating could significantly improve the degradation properties of magnesium alloy. The pH of the solution containing the coated samples increased much more slowly than the untreated control. After 8 d immersion, the uncoated sample had corroded seriously while the coated sample was much less corroded. The Ca/P atom ratio in both the layers of the coating increased and the coating was still protecting the substrate. The two layers of the coating corroded differently because of differences in solubility. The outer layer was more severely attacked and many holes were formed on the surface, the inner layer suffered less attack. In addition, a growth of precipitate on the inner layer was observed, indicating that surface bioactivity was improved by the coating. Thus, magnesium alloys coated with a Ca-P coating prepared by a hydrothermal method are promising candidate biodegradable biomaterials, and further investigation of in vivo degradation behavior is suggested.

Reduction of the biodegradation rate of MgZnSrCa alloy by use of a biomimetic apatite coating

Preparing Ca-P Coating on Biodegradable Magnesium Alloy by Hydrothermal Method: in Vitro Degradation Behavior

Controlling the Degradation Rate of Biodegradable Mg–Zn-Mn Alloys for Orthopedic Applications by Electrophoretic Deposition of Hydroxyapatite Coating

Surface Engineering of Biodegradable Magnesium Alloys for Enhanced Orthopedic Implants.

Characterization and Degradation Study of Calcium Phosphate Coating on Magnesium Alloy Bone Implant in Vitro

Recent Advances on Development of Hydroxyapatite Coating on Biodegradable Magnesium Alloys: A Review

Tailoring Biodegradation of Mg-Ca Alloy by Acid Pickling and Polydioxanone/n-Hydroxyapatite Composite Coating for Temporary Implant Applications

In vivo degradation and bone formation behaviors of hydroxyapatite-coated Mg alloys in rat femur

Optimization of the in Vitro Biodegradability, Cytocompatibility, and Wear Resistance of the AZ31B Alloy by Micro-Arc Oxidation Coatings Doped with Zinc Phosphate

Polydopamine mediated assembly of hydroxyapatite nanoparticles and bone morphogenetic protein-2 on magnesium alloys for enhanced corrosion resistance and bone regeneration

Biodegradable Magnesium Bone Implants Coated with a Novel Bioceramic Nanocomposite

In Vivobiocompatibility and Degradation Behavior of Mg Alloy Coated by Calcium Phosphate in a Rabbit Model

Evaluating the Electrochemical and In Vitro Degradation of an HA-Titania Nano-Channeled Coating for Effective Corrosion Resistance of Biodegradable Mg Alloy

Advances in hydroxyapatite coatings on biodegradable magnesium and its alloys

A Study on the Structure and Biomedical Application Characteristics of Phosphate Coatings on ZKX500 Magnesium Alloys

Calcium Phosphate Coating on Magnesium Alloy for Modification of Degradation Behavior

In Vitro and in Vivo Studies on As-Extruded Mg- 5.25Wt.%zn-0.6Wt.%ca Alloy As Biodegradable Metal

Enhanced Biocompatibility and Osteogenic Property of Biodegradable Zn-0.5Li Alloy through Calcium–Phosphorus Coating

Effect of Strontium-Substituted Calcium Phosphate Coatings Prepared by One-Step Electrodeposition at Different Temperatures on Corrosion Resistance and Biocompatibility of AZ31 Magnesium Alloys

Osteochondroma of the convexity: pathologic-neuroimaging correlates of a lesion that mimics high-grade meningioma

Biodegradable and Bioactive Orthopedic Magnesium Implants with Multilayered Protective Coating.