Abstract:Fabric made of polyethylene terephthalate (PET) is a common textile that is widely used in daily life. Its flame retardancy has emerged as a major concern for lowering the risk of fire. As a kind of popular flame retardants, cyclic phosphoramides have been widely applied to improve the flame retardancy of various inflammable materials. To achieve more suitable and effective flame retardants for PET fabric, the fire-safety capabilities of PET fabric coated with various cyclic phosphoramides substituted by siloxane (PDPTP), hydroxyphenyl (DPHBP), and hydroxyethyl (PDNP) groups was explored in this work. All of these chemicals can successfully prevent PET fabric from melting and burning, providing it good flame retardancy and non-dripping performance. LOI values for PET fabrics coated with PDPTP, DPHBP and PDNP increased to 24.6, 25.2, and 30.3% under comparison loadings. These flame-retardant coatings enhanced the char-forming capacity for PET fabric. The residues at 700 °C increased to 26.5 and 27.4% for PDPTP and PDNP coated fabric in N2 atmosphere compared with 2.9% for pure fabric. Peak heat release rate (PHRR) and total heat release (THR) was effectively restrained by 50% and 35%, respectively. Fortunately, these flame-retardant coatings had no detrimental effects on the mechanical characteristics of PET fabric and even enhanced the weft's tensile breaking forces. Apart from DPHBP significantly reducing the fabric's whiteness, the whiteness of PDPTP and PDNP coated PET fabric hardly changed. The effect of cyclic phosphoramides with various substitutions on the flame retardancy of PET fabric is thoroughly discussed in this paper, which might be useful in the development of more effective flame retardants for PET materials.

Fabrication of Montmorillonite and Titanate Nanotube Based Coatings Via Layer-by-layer Self-Assembly Method to Enhance the Thermal Stability, Flame Retardancy and Ultraviolet Protection of Polyethylene Terephthalate (PET) Fabric

Application Of Poly(Diphenolic Acid-Phenyl Phosphate)-Based Layer By Layer Nanocoating In Flame Retardant Ramie Fabrics

Liquid Crystalline Pet/60hba-Mwnts Composite: Synthesis, Characterization, and Properties

Fully bio-based flame retardant and antibacterial coating for polyethylene terephthalate fabric

Polyethylene Terephthalate Composite Films with Enhanced Flame Retardancy and Gas Barrier Properties via Self-Assembly Nanocoating

Fabrication of transparent clay-polymer hybrid coatings on PET film to enhance flame retardancy and oxygen barrier properties

Durable flame retardant treatment of polyethylene terephthalate (PET) fabric with cross-linked layer-by-layer assembled coating

Environmental benign foam finishing with a hyperbranched polyphosphonate flame retardant for polyethylene terephthalate fabric

Flame Retardancy and Non-Isothermal Crystallization Behaviour of Pet/Tio2 Nanocomposites

Preparation of TiO2-NT Coated PET Fabrics and Their Formaldehyde Degrading Effect

Flame retardant and anti-dripping polyethylene terephthalate fabric based on bio-based phytic acid/gelatine coating

Durable flame retardant and anti-dripping of PET fabric using bio-based covalent crosslinking intumescent system of chitosan and phytic acid

Scalable Preparation of Superdurable, Self-Healing, and Biocompatible Superhydrophobic Poly(ethylene terephthalate) Fabrics

N-substituted cyclic phosphoramides as flame-retardant and anti-dripping coatings for PET fabric

In-Situ Formation Of Bhet/Titanium Compound Nanocomposite And Its Catalysis For Polyester

Preparation and characterization of poly(ethylene terephthalate) fabrics treated by blends of cellulose nanocrystals and polyethylene glycol

Fabrication of Multifunctional PET Fabrics with Flame Retardant, Antibacterial and Superhydrophobic Properties

Antistatic Poly(Ethylene Terephthalate)/Polyaniline-Coating Multiwalled Carbon Nanotubes Nanocomposites

Construction of layer-by-layer assembled chitosan/titanate nanotubes based nanocoating on cotton fabrics: flame retardant performance and combustion behavior

Fabrication of Polyethyleneimine and Poly(styrene-<I>alt</I>-maleic Anhydride) Nanotubes Through Covalent Bond

Flame Retardancy of Poly(Ethylene Terephthalate) Nanocomposites Based on Rare Earth Ions Modified Organo-Montmorillonite