Abstract:Polyester fabric is ubiquitously applied for clothing, furniture and transportation, whereas its flammability with severe dripping often causes secondary hazards. Herein, it is highly imperative to impart excellent flame retardant to polyester fabric. In this work, a coating for polyester fabrics was prepared through a continuous dipping and ultraviolet (UV) curing process, which exhibited high-efficiency flame-retardant, anti-dripping and washing resistance. Firstly, the surface of polyester fabric was pretreated with plasma for providing more grafting sites of polyester fabric. Then, the flame retardant 6-((((2-(acryloyloxy) ethoxy) (oxo)(phenyl)phosphonio) oxy) methyl) dibenzo[c,e][1,2]oxaphosphinine 6-oxide (DPEA) and Tri(acryloyloxyethyl) phosphate (TAEP) were successfully synthesized and applied to the coating by UV-curing. In vertical burn test, the damage length of polyester with DPEA and TAEP (PET-D3/T4.5) was reduced from 300 mm of pristine PET to 100 mm with no dripping. In the Thermogravimetric Analysis (TGA) test, the char residue of PET-D3/T4.5 in nitrogen increased to 26.7 % compared with 9.7 % of pristine polyester. More specifically, the Peak Heat Release Rate (PHRR) and Total Heat Rate (THR) of PET-D3/T4.5 decreased 43.3 % and 22.2 % in the Micro-scale Combustion Calorimetry (MCC) test, which reflected excellent thermal stability and flame retardant properties. In addition, the Limiting Oxygen Index (LOI) of PET-D3/T4.5 only dripped from 24 % to 23.5 % after ten standard laundering cycles, indicating prominent water resistance. Remarkably, Thermogravimetric Analysis-Fourier transform infrared (TG-IR), Scanning Electron Microscope (SEM) and X-ray Photoelectron Spectroscopy (XPS) have been performed for investigating the mechanism of flame retardant. Thus, a strategy with convenience and economics is proposed, which is of gargantuan significance to the improvement of coating durability through plasma surface treatment and UV-curing.

Durable flame retardant and anti-dripping of PET fabric using bio-based covalent crosslinking intumescent system of chitosan and phytic acid

Fully bio-based flame retardant and antibacterial coating for polyethylene terephthalate fabric

Flame retardant and anti-dripping polyethylene terephthalate fabric based on bio-based phytic acid/gelatine coating

Durable flame retardant treatment of polyethylene terephthalate (PET) fabric with cross-linked layer-by-layer assembled coating

A flame-retardant PET fabric coating: Flammability, anti-dripping properties, and flame-retardant mechanism

N-substituted cyclic phosphoramides as flame-retardant and anti-dripping coatings for PET fabric

Environmental benign foam finishing with a hyperbranched polyphosphonate flame retardant for polyethylene terephthalate fabric

Construction of bio‐safety flame retardant coatings on polyethylene terephthalate fabric with ammonium phytate and cyclodextrin

Construction of durable flame retardant, anti-dripping, and smoke-suppressing recycled polyester fabric

Preparation of flame retardant and anti-dripping PET fabric based on sodium copper chlorophyllin dyeing, UV grafting and phosphorylation

A highly thermostable flame retardant for poly(ethylene terephthalate) and its fabric with satisfactory comprehensive flame retardancy

Construction of a durable superhydrophobic flame-retardant coating on the PET fabrics

Preparation of dyeing, flame retardant and anti-dripping polyethylene terephthalate fibers based on natural sodium copper chlorophyll dyeing and intercalation of phosphorylated sucrose fatty acid ester

Preparation of Siloxane-Modified DOPO Flame Retardant Sol–Gel and Its Study on Flame Retardant PET Fabrics

Preparation of a copper porphyrin derivative and its surface modification for simultaneously endowing PET fibers with dyeing, flame retardant and anti-dripping performance

Bio-based flame retardant coatings for polyester/cotton fabrics with high physical properties using ammonium vinyl phosphonate-grafted chitosan complexes

Durable flame retardant and dip-resistant coating of polyester fabrics by plasma surface treatment and UV-curing

Metal compounds as catalysts in the intumescent flame retardant system for polyethylene terephthalate fabrics

A phosphorous/nitrogen-containing flame retardant with UV-curing for polyester/cotton fabrics

Toward a Sustainable Approach for Durably Hydrophilic and UV Protective PET Fabric through Surface Activation and Immobilization Integrating Epigallocatechin Gallate and Citric Acid