Oil-water Self-Assembly Synthesis of Ag@AgCl/K4 Nb6 O17 and Enhanced Photocatalytic Degradation of Organic Pollutants

ZHAO Junxiu,LIU Li,HU Jinshan,LIANG Yinghua,CUI Wenquan

DOI: https://doi.org/10.3969/j.issn.1001-9731.2015.12.009

2015-01-01

Abstract:The composite photocatalyst of Ag@AgCl/K4 Nb6 O17 was composed of by the oil-water self-assembly method,on the basis that K4 Nb6 O17 was prepared in the high-temperature solid-state method.The microstruc-ture,morphology and properties of Ag@AgCl/K4 Nb6 O17 composite photocatalyst were characterized by means of XRD,SEM,TEM,EDX,UV-vis,PL,BET;and the photocatalytic performance was valued by the degra-dation of methylene blue (MB),phenol,and Rhodamine B (RhB)under visible light irradiation.The results shows that Ag@AgCl particles with the size of about 20 nm were dispersed in two-dimensional layer structure on the surface of K4 Nb6 O17 and the absorption of visible light of the composite photocatalyst ranged from 400 to 800 nm due to the surface plasmon resonance of Ag.The degradation rate of MB solution over Ag@AgCl (25wt%)/K4 Nb6 O17 under the visible light irradiation reaches 88.2% in an hour,which is more than two times compared with the sum of the Ag@AgCl and K4 Nb6 O17 degradation rate.The composite photocatalyst still ex-hibited high catalytic activity after recycled five times,and photocatalytic activities for the degradation of phenol and RhB were also observed.The degradation mechanism of Ag@AgCl/K4 Nb6 O17 composite photocatalyst was proposed.