Photocatalytic and photochemical processes of AgCl/TiO2 studied with a fully integrated X-ray photoelectron spectrometer
Kai Zhou,Wen-Lu He,Xiao Zhang,Bin Zhang,Xiang-Nan Gong,Kai-Wen Wang,Zhi-Chao Zhang,Xi-Lan Zhang,Zhi-Ning Xia,Xiao-Yuan Zhou
DOI: https://doi.org/10.1007/s12598-020-01635-7
IF: 6.318
2021-01-07
Rare Metals
Abstract:<span class="a-plus-plus abstract-section id-a-sec1"><p class="a-plus-plus">A fully integrated X-ray photoelectron spectrometer (XPS) was employed for the investigation of the separation processes and recombination behaviors of photogenerated electrons and holes on the surface of AgCl and ultra-small nano-titanium oxide cluster composite photocatalyst (AgCl/TiO<sub class="a-plus-plus">2</sub>). A facile route, by direct colloidal synthesis, for preparing AgCl/TiO<sub class="a-plus-plus">2</sub> with high stability and enhanced visible light (Vis) driven catalytic activity was reported. The photocatalytic activity of AgCl/TiO<sub class="a-plus-plus">2</sub>, which revealed that the photo-degradation rate of the as-prepared AgCl/TiO<sub class="a-plus-plus">2</sub> was nearly 10.5 times higher than that of bare AgCl, was evaluated by applying it to the photo-degradation of methyl orange (MO) in water solution. Moreover, AgCl/TiO<sub class="a-plus-plus">2</sub> exhibited an outstanding long-term stability during ten cycles of photo-degradation. The band gap of AgCl decreased from 3.25 to 2.85 eV because of the ultra-small nano-TiO<sub class="a-plus-plus">2</sub> clusters that were pinned to its surface. The results indicate that the band gap narrowing and surface plasmon resonance (SPR) of Ag (0) were two major contributors to the enhancement of the photocatalytic activity of AgCl/TiO<sub class="a-plus-plus">2</sub> by improving the utilization of Vis. In situ XPS analysis was, therefore, certified as a beneficial method to explore the catalytic mechanism of photocatalysts.</p></span><span class="a-plus-plus abstract-section id-a-sec2 outputmedium-online"><h3 class="a-plus-plus">Graphic abstract</h3></span>
materials science, multidisciplinary,metallurgy & metallurgical engineering