Preparation and Characterization of Antibacterial Oxide Film with Deposited Silver on Al Alloy
Jing Bai,Yue Zhang,Chuanmeng Xu,Chao Sun,Huan Liu,Mengmeng Lu,Yi Shao,Chenglin Chu,Feng Xue
DOI: https://doi.org/10.1088/2053-1591/ac2930
IF: 2.025
2021-01-01
Materials Research Express
Abstract:Aluminum (Al) alloy products are widely used in people’s lives, while the existence and breeding of microorganisms on their surface cannot meet the health criteria and even may harm human health. In the present study, we successfully prepared the antibacterial oxide film on the 6063 Al alloy specimens by direct-current anodizing followed by Ag element depositing and the hole sealing process. The results suggested that compared with the Al substrate, the wear resistance of the obtained film was increased to 0.79, and the corrosion resistance was significantly improved. The antibacterial rate against Escherichia coli could be achieved as 94.38 ± 3.23%, and the adhesion force between the film and substrate was about 11 N. With the increase of the deposition time, the surface color of samples was gradually darkened, and meanwhile, the surface became uniform again without particles eventually. Energy dispersive spectroscopy (EDS) results showed the silver element was deposited on the surface and at the bottom of the porous oxide layer, and the amount of silver also increased with prolonging the deposition time. Moreover, x-ray photoelectron spectroscopy (XPS) analysis results on the surface showed the deposited silver element existed in the form of the ion and elemental substance, which indicated that reduction reaction of Ag+ appeared on the oxide film surface.