Repair of segmental bone defects in rabbit radii with tissue-engineered bionic artificial bone
Kai Lian,Yun-yu Hu,Gang Liu,JQ Xu,Z Yuan,R Lü,JP Bai,L Sun
DOI: https://doi.org/10.3321/j.issn:1673-8225.2007.06.005
2007-01-01
Abstract:AIM: To study the efficacy of porous bionic artificial bone loaded with autologous bone marrow stromal cells (BMSCs) on the healing of rabbit's radial segmental bone defects. METHODS: The experiment was carried out in the Institute of Orthopaedics, Xijing Hospital, the Four Military Medical University of Chinese PLA from January 2002 to May 2003.①Autologous BMSCs were isolated from bone marrow of adult rabbits, grown and induced in culture.②The osteoblasts were loaded onto porous scaffolds consisting of nano-hydroxyapatite/collage (NHAC, 4∶1) and poly (L-lactic acid) (PLLA, 1∶1), porosity > 90%; pore 50-300 μm; specification 15 mm×3 mm×3 mm. Before use, a series of managements such as ethanol, double distilled water and centrifugalization. The BMSCs at passage 3 were co-cultured in the above materials, 3×1010 L-1. A compound of BMSC and bionic matrix material was established in vitro.③An experimental model of 15-mm bone defect was made in the right radius of rabbits, the animals were randomly divided into three groups. In the experimental group (n =14), a porous NHAC/PLLA scaffold that had been loaded with autologous BMSCs was implanted in the defect. In the control group (n =14), a scaffold that had not been loaded with cells was placed in the defect. In the blank group (n =6), the defect was untreated. A series of examinations including radiography, bone mineral density measurement, histological and histomorphometic studies were carried out to assess the repairing capability of the defects. RESULTS: All 34 rabbits were involved in the result analysis.①Co-culture in vitro: Rabbit BMSCs got almost confluence on day 7, with collagen fibrils occurring on the surface of cells or around them.②X-ray examination: In the experimental group, bone defects at higher bone mineral density were entirely healed by 24 weeks with almost equivalent images of normal radius. In the control group, minimal amounts of callus were only observed in the areas adjacent to the cut ends of host bone, but no continued callus formed on the surface of materials. In the blank group, non-union was seen in the defects with the cut ends sclerosed.③Bone mineral density examination: In the experimental group, bone mineral density of defects was much higher than that in the control groups at weeks 16 and 24 [16 weeks: (0.152±0.041), (0.092±0.029) g/cm2; 24 weeks: (0.177±0.044), (0.113±0.026) g/cm2, t =2.67, 2.80, P < 0.05], with no difference to collateral normal radius.④Histological evaluation: In the experimental group, osteogenesis was present in the areas of bone defects with scaffolds almost degraded at week 24. In the control group, the centre of defects was filled with fibrous. Scaffolds partly degraded into particles. Only both ends of them showed new bone tissues. In the blank group, no bone formation was observed in the areas of bone defects.⑤Histomorphometic study: In the experimental group, the percentage of new bone formation was increased with the time extended and was significantly higher than that seen in the control group at weeks 8, 16, 24 (t =8.971, 11.240, 12.836, P < 0.01). CONCLUSION: ①Autologous BMSCs with osteogenic potential may be harvested by micro-invasive method, and the implantation of porous NHAC/PLLA scaffold composites into BMSCs can quickly elicit the healing process of bone defects.②The tissue engineering approach is effective in the repair of segmental bone defects, and may be an alternative to bone-grafting in clinic.