Abstract:The size effect in the fracture of solids represents a highly critical issue with a prolonged history of research. The size effect of traditional quasi-brittle materials can already be well described through the size effect model. However, there is still a lack of research on the size effect of strain-hardening cementitious composites (SHCC), a special type of fibre-reinforced concrete with macro-scale strain-hardening behaviour after first cracking. Being distinct from traditional quasi-brittle materials with softening nature, SHCC is thus expected to behave differently in terms of size effect. In this research, the structural size effect problem of SHCC is comprehensively studied by experimental investigation and theoretical analysis. Geometrically similar notched three-point bending specimens were tested in mode I and mixed mode I/II fracture condition. The whole-process of failure and matrix cracking zone around the main crack was captured with high resolution by digital image correlation technology. Experimental results showed that apparent fracture energy, nominal strength, structural ductility and fracture resistance curve are all structural size-dependent. The apparent fracture energy was shown to arise with specimen size within the tested range. This is related to large-scale pseudo yielding, i.e. enlargement of matrix cracking zone (like the yielding zone in metals) with increasing structural size. It thus provides an indirect method for the estimation of cohesive fracture energy of single crack with constitutive nature. Due to the scaled matrix cracking zone, an intermediate asymptote exists in the size effect curve of nominal strength, in addition to the plastic and LEFM asymptotes in the Bažant original size effect law. This resembles the recent finding of intermediate asymptote in plastic-hardening metal( Dönmez et al. 2023 ). The size-dependence of R-curve was also examined. Though size-dependent, the equivalent LEFM-based R-curves are shown to have three common stages reflecting different cracking processes. Based on experimental results, the size effect of fracture energy and nominal strength are finally modelled theoretically in the Bažant's framework of equivalence between energy release and fracture resistance.

EFFECTS OF SPECIMEN SIZES ON THE LOCAL CLEAVAGE FRACTURE STRESS OF STEEL

Effects Of Notch Geometry On The Local Cleavage Fracture Stress Sigma(F)

Study on Ultra‐low Cycle Fatigue Fracture of Thick‐walled Steel Bridge Piers

Experimental and Theoretical Investigation of Size Effects on the Ductile/Brittle Fracture Toughness of A Pressure Steel

Size effects on the ductile/brittle fracture properties of the pressure vessel steel 20 g

Experimental Investigation of the Size Effects on the Fracture Toughness and Tearing Modulus

Size effect on fracture behavior of quasi-brittle materials during uniaxial compression tests

Fracture of 0.1 and 2 M Long Mortar Beams under Three-Point-bending

Structural size effect in the mode I and mixed mode I/II fracture of strain-hardening cementitious composites (SHCC)

Statistical characterization of specimen size and temperature dependence of cleavage fracture toughness of ferritic steels

Effect of crack size, thickness and span on the transverse mode I fracture characteristics of laminated flattened-bamboo lumber

Fracture Behavior and Size Effect of UHPFRC: Experimental and Mesoscale Numerical Investigation

In-depth Analysis of Notched 3-P-b Concrete Fracture

Boundary Element Simulation of Size Effect for Quasi-Brittle Materials by Using One-Size Specimen

Study on Fracture Toughness Indices of Chinese Structural Steel and Weld Metal

Experimental Description of Size Effect for Brittle Materials Using Specimens with Fixed Crack Length

A Weibull distribution-based method for the analysis of concrete fracture

An investigation on fracture toughness predictions from mini-sized uniaxial tensile specimens with global and local approaches

Effects of notch width and loading rate on the dynamic mode II fracture toughness of Ti-6Al-4V

Research on size effect of fracture toughness of sandstone using the center-cracked circular disc samples

Numerical Analysis of Effect of Specimen's Geometric Size and Bar's Material on Testing Result for CCCD-SHPB Dynamic Fracture Test System