Synthesis and Phase Structure of Poly(Vinylidene Chloride-co-Methyl Acrylate)-b-Poly(Butyl Acrylate) Copolymers

WANG Fei-fan,BAO Yong-zhong

DOI: https://doi.org/10.3969/j.issn.1003-9015.2016.01.025

2016-01-01

Abstract:Poly(vinylidene chloride-co-methyl acrylate)-b-poly(butyl acrylate)(P(VDC-co-MA)-b-PBA) copolymers with different compositions were synthesized by a reversible addition fragmentation-chain transfer(RAFT) emulsion copolymerization method, and their phase structures and thermal weight loss behaviors were investigated. The results showed that stable P(VDC-co-MA) and P(VDC-co-MA)-b-PBA copolymer latexes could be prepared using 2-(dodecylthiocarbonothioylthio)-2-methylpropionic acid terminated amphiphilic poly(acrylic acid)-b-polystyrene copolymer as a chain transfer agent(CTA) and emulsifier, and hexadecane as a costabilizer. The number average molecular weights of P(VDC-co-MA) and P(VDC-co-MA)-b-PBA copolymers increased as the molar ratio between CTA and monomer(s) decreased, which indicated the living nature of polymerization. P(VDC-co-MA)-b-PBA copolymer films prepared by solution casting and latex coating exhibited micro-phase separated morphology. When the molar ratio between P(VDC-co-MA) and PBA blocks increased from 11/1, 2.2/1 to 1/1, the morphology changed from PBA dispersed as sphere domains to PBA dispersed as thread domains, and then to bi-continuous phase structures. The P(VDC-co-MA)-b-PBA copolymers showed two thermal weight loss peaks corresponding to P(VDC-co-MA) and PBA.