Study on in-situ Modification of Vinyl Acetate-Acrylate Latex by Anatase TiO2 Sol
Zong Jianjuan,Shen Qianhong,Xiang Zhenmao,Li Sheng,Zhou Jian
2010-01-01
Rare Metal Materials and Engineering
Abstract:With TiOSO4 as raw materials stable anatase TiO2 sol was prepared. The sol was prepared was added into vinyl acetate-acrylate latex, to in-situ the composite emulsion containing nano crystalline TiO2. The film was prepared by a dip-coating method from the above emulsion. XRD, TEM and SEM were adopted to characterize the phase structure of TiO2 sol, the size and shape of particles in the composite emulsion and the surface morphology of the film. The effect of TiO2 addition amount on the contact angle, surface morphology and photocatalytic performance of the film were also investigated. The results show that the composite emulsion has high stability and excellent film forming property, and TiO2 particles are well distributed in the composite film. With the increase of TiO2 sol addition amount, TiO2 particles in the surface of the film are increased, leading to the increase of roughness of the film. After the UV irradiation, the contact angle of composite film decreases with the increase of TiO2 sol addition amount, and the photocatalytic performance is gradually improved.