Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Low Cycle Fatigue Behavior of Squeeze Cast Al-7.1Zn-2.4Mg-2.1Cu-0.55Fe Alloy

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of Fe content on low cycle fatigue behavior of squeeze cast Al-Zn-Mg-Cu alloys

A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

Low cycle fatigue response and fracture mechanism in a novel Al-3.5Si-0.5Mg-0.4Cu casting alloy

Hot tensile and fatigue behaviour of zinc–aluminum alloys produced by gravity and squeeze casting

Cyclic Deformation Behavior of A Heat-Treated Die-Cast Al-Mg-Si-Based Aluminum Alloy

High-Cycle Fatigue of Mg–6Gd–3Y–0.5Zr Cast Magnesium Alloys

Microstructure and mechanical properties of squeeze-cast Al−5.0Mg−3.0Zn−1.0Cu alloys in solution-treated and aged conditions

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Experimental study of squeeze casting of ZK60 magnesium alloy

Developing high performance squeeze cast Al-Cu alloys with high Fe and Cu contents

Anisotropic Low Cycle Behavior of the Extruded 7075 Al Alloy

High Cycle Fatigue Properties of Die-Cast Magnesium Alloy Az91d-1%Mm

High-cycle fatigue failure analysis of cast Al-Si alloy engine cylinder head

Developing High Performance Mechanical Properties at Elevated Temperature in Squeeze Cast Al-Cu-Mn-Fe-Ni Alloys

On the Failure Mechanism for High Pressure Die Casting A390 Hypereutectic Alloy in Low Cycle and High Cycle Fatique

Effect of Precipitation-Free Zone on Fatigue Properties in Al-7.02Mg-1.98Zn Alloys: Crystal Plasticity Finite Element Analysis

Relationship Between the Fatigue Behavior and Grain Structures of an As-Extruded Mg-6.2%Zn-0.6%Zr (in Wt.%) Alloy

Experimental Investigation and FE Analysis on Constitutive Relationship of High Strength Aluminum Alloy under Cyclic Loading

Role of defects on the high cycle fatigue behavior of selective laser melted Al–Mg–Sc–Zr alloy