Morphology, phase composition, surface roughness evolution and growth mechanism of hot-dip aluminum coating on Mo substrate
Tao Fu,Yingyi Zhang,Zhichen Han,Luyu Chen,Junjie Zhu,Shiheng Peng
DOI: https://doi.org/10.1016/j.jmrt.2023.12.077
IF: 6.267
2023-12-17
Journal of Materials Research and Technology
Abstract:The Al-rich hot-dip aluminum composite coatings were synthesized on Mo surface by hot-dip aluminizing under different deposition processes. The aluminide coatings present a very smooth dense coating structure with a lower surface roughness and fine grain size, the average surface roughness (RSa) values are only 0.118–0.869 μm, and the corresponding surface area growth rate (Sdr) values are 3.85–80.19 %. Increasing the deposition temperature is beneficial for the transition of low melting point compounds of the coating surface to high melting point compounds, and extending the hot dip time is profit for the diffusion and enrichment of Al atoms on the coating surface. Besides, increasing the deposition temperature or time can also promote the growth of Al 4 Mo grains, thereby significantly increasing the coating thickness. When the deposition temperature is 750 °C, the thicknesses of Al 4 Mo and Al 8 Mo 3 layers increases in a parabolic law with deposition time, and the K p values both of them are 3.46 × 10 −13 m 2 /s and 1.47 × 10 −15 m 2 /s, respectively. The growth of the coating depends on the continuous diffusion of Al atoms towards the substrate direction, and the difference in chemical potential between Al atoms in each phase is the main driving force for coating growth.
materials science, multidisciplinary,metallurgy & metallurgical engineering