Synthesis of UV- Curing Polyamidoamine Dendrimer Resin
Hu Jiajuan,Guo Xiusheng,Yu Demei,Su Minru,Guo Rongnan
DOI: https://doi.org/10.3969/j.issn.0253-4312.2011.11.002
2011-01-01
Abstract:A series of polyamidoamine(PAMAM)dendrimer from 0.5 generation to 3.5 generation have been synthesized by divergent method.Half generation of PAMAM(0.5G,1.5G,2.5G,3.5G)were hydrolysised in acidic conditions.The compositions and structures of half generation of PAMAM and its hydrolyzed products were characterized by means of FT-IR and~1H NMR.The hydrolyzed products were modified with hydroxyethyl acrylate to form a UV-curable polyamidoamine dendrimer which couled be cured under UVlight without diluent.Film surface was smooth,soft,uniform color,no air bubbles inside and showed a better apparent performance,solving the problem that a lot of thinner needed to be added in order to reduce the viscosity of polymer materials.FT-IR proved the success of modification.The properties of the modified resin were tested,such as solubility(U V-curable resin ),melting point and heat stability(UV-curable film). The property of the different generation products were researched.The solubility of modified PAMAM had a great change after hydrolysis,which could only be dissolved in many strong polar solvents,for example,water, methanol and N,N-dimethyl formamide.DSC test showed that the melting point of the UV-curable film was decreased with the increase of generation.TG analysis showed that the thermal decomposition reaction of the UV-curable film was a stepwise process from the outer to the inner.Temperature of initial decomposition of film was above 170 ℃ ,showing a good heat stability.