Application of X-ray Rietveld Method in the Cement

Yan-ling GAN,Tou-nan JIN,Guang-lin NIE,Su-ping CUI,Jun GUO

DOI: https://doi.org/10.16552/j.cnki.issn1001-1625.2015.07.013

2015-01-01

Abstract:X-ray Rietveld method and TOPAS software were used for quantitative analysis of phases in Portland cement,and the influence of Al2( SO4)3·18H2O which can be as the coagulant on the hydration products of portland cement was studied by X-ray Rietveld method. The results showed that,crystal phase contents of reference cement were 9. 391% for C2 S,48. 615% for C3S,2. 749% for C3 A,9. 493% for C4 AF and 26. 782% for amorphous phase. The proportion of amorphous phase was relatively high and cannot be neglected. Compared with the blank test without Al2(SO4)3·18H2O,adding 1%Al2( SO4)3·18H2O could make the residual amount of C3S reduce by 5. 25% and the production of ettringite increase by 30. 69% in the 1d hydration products,so the hydration of the cement was promoted and the 1d compressive strength was increased by as much as 9. 24% with 1% Al2( SO4)3·18H2O.However,adding 4% Al2( SO4)3·18H2O made the residual amount of C3S increase by 15. 17% and the production of C-S-H reduce by 22. 38% in the 1d hydration products,so the hydration of C3 S was suppressed and the 1d compressive strength with 4% Al2( SO4)3·18H2O was lower than the 1 d compressive strength with 1% Al2( SO4)3·18H2O. 1% and 4% Al2(SO4)3·18H2O could make the residual amount of C3 S 3. 19%,6. 22% respectively higher than the blank test in the 28 d hydration products,the production of ettringite increased by 64. 40%,191. 50% respectively. So the hydration of C3 S was suppressed,and the 28 d compressive strength of cement paste decreased.