Abstract:Objective: The aim of this article was to evaluate the effects of modifying glass ionomer cement (GIC) with carboxymethyl chitosan (CMC) on surface morphology and remineralization outcomes by examining dentin morphology and calcium ion composition changes. Materials and methods: Thirty holes in a cylindrical acrylic mold were filled with three groups of restorative materials: GIC, GIC modified with CMC (GIC-CMC) 5%, and GIC-CMC10%. The surface morphology of each group's materials was observed using scanning electron microscopy (SEM). The compressive strength measurement was performed using a universal testing machine. The dentin remineralization process was performed by applying GIC, GIC-CMC5%, and GIC-CMC10% materials for 14 days on demineralized dentin cavities treated with 17% ethylenediamine tetraacetic acid (EDTA) for 7 days. A morphological evaluation was conducted using SEM. The calcium ion composition and calcium-to-phosphorous (Ca/P) ratio were examined using an energy-dispersive X-ray (EDX). Statistical analysis: The Kruskal-Wallis and post-hoc Mann-Whitney U tests were performed to compare all four groups of calcium ions (p < 0.05). Results: The modification of GIC with CMC affected the morphological changes in the materials in the form of reduced porosity and increased fractures. A significant difference was found in compressive strength between the GIC-CMC modification materials of GIC-CMC5% and GIC-CMC10% and the GIC control group. The dentin tubule morphology and surface changes were observed after applying GIC, GIC-CMC5%, and GIC-CMC10% materials for 14 days, as evaluated by SEM. The EDX examination showed an increase in calcium ion content and hydroxyapatite formation (Ca/P ratio) after applying the GIC-CMC10% material. Conclusion: The surface porosity of the GIC modification material with the addition of CMC tended to decrease. However, an increase in cracked surfaces that widened, along with the rise in CMC percentage, was found. This modification also reduced the compressive strength of the materials, with the lowest average yield at 10% CMC addition. Therefore, the modification of GIC with CMC affects changes in morphology, calcium ion composition, and Ca/P ratio in demineralized dentin.

The Effect of Reducing Amalgam Microleakage with Glass Ionomer Cement in Vitro

Effect of a novel glass ionomer cement containing fluoro-zinc-silicate fillers on biofilm formation and dentin ion incorporation

Effect of Silver Diamine Fluoride and Potassium Iodide Treatment on Secondary Caries Prevention and Tooth Discolouration in Cervical Glass Ionomer Cement Restoration

[The effect of cavity finishing on the initial sealing capacity of amalgam fillings in vitro]

Effect of desensitizer on the microleakage of wedge shaped defects after filling

An in Vitro Evaluation of Coronal Microleakage of Five Temporary Restorative Materials Used in Endodontic Access Cavities

Fluoride release and uptake by glass-ionomers and related materials and its clinical effect

Comparative Evaluation of Microleakage of Fiber-reinforced Glass Ionomer Cement and Conventional Glass Ionomer Cement Restorations Immersed in Three Different Beverages: In Vitro Study

Nano-cellulose Reinforced Glass Ionomer Restorations: An In Vitro study

Effectiveness of different resin composite materials for repairing noncarious amalgam margin defects

Preventing proximal enamel caries in neighboring tooth with glass ionomer cement restoration and silver diamine fluoride pretreatment

Experimental Research of Effect of Removal of the Smear Layer on Apical Microleakage

Inhibitive Effect of a New Dental Resin Composite on Enamel Artificial Caries

Environmental degradation of glass-ionomer cements: A depth-sensing microindentation study

Microhardness evaluation of enamel adjacent to an improved GIC sealant after different enamel pre-treatment procedures

Glass ionomer cement inhibits secondary caries in an in vitro biofilm model

Comparative evaluation of microleakage between bulk esthetic materials versus resin-modified glass ionomer to restore Class II cavities in primary molars

Comparation of the Clinical Effects of Glass Ionomer Cement and Flowable Composite Resin on the Restoration of Dental Wedge-Shaped Defects

Evaluation of Microleakage Using Different Luting Cements in Kedo Zirconia Crowns: An In Vitro Assessment

Evaluation of Physical Properties in Carboxymethyl Chitosan Modified Glass Ionomer Cements and the Effect for Dentin Remineralization: SEM/EDX, Compressive Strength, and Ca/P Ratio

PENETRATION OF AMALGAM CORRODED PRODUCTS INTO DENTIN AND ITS EFFECT ON BONDING USING SELF ETCH ADHESIVE SYSTEM VERSUS RESIN MODIFIED GLASS IONOMER