Synthesis and Characterization of Linear and Star-shaped Carboxyl Acid-Terminated Polydimethylsiloxane
YAN Li-shan,LIN Ya-ling,QIU Yuan-huan,ZOU Jie,WANG Dan,LIN Fang,ZHANG An-qiang
DOI: https://doi.org/10.3969/j.issn.1009-4369.2013.02.002
2013-01-01
Abstract:A three-step procedure was developed for synthesizing a series of linear and star-shaped car-boxyl-terminated polydimethylsiloxane , i.e., PDMS-MAAx (x=1, 2, 3, 4).First, the hydrogen-termina-ted PDMS with virous arms (PDMS-Hx ) were prepared based on the ring-opening polymerization of octam-ethylcyclotetrasiloxane (D4 ); then, methyl methacrylate (MMA) was reacted with PDMS-Hx to prepare es-ter terminated PDMS (PDMS-MMAx );finally, the terminal ester group was transformed to terminal carboxyl acid based on the hydrolysis reaction of ester under alkaline condition to obtain carboxyl acid terminated PDMS, i.e., PDMS-MAAx .FT-IR and 1 H NMR were employed to confirm the structure of the product in each step of reactions and the effects of synthetic conditions on the structure of the products were discussed . Also, the optimal conditions for the preparation of PDMS -MMAx were with a mole ratio of Si-H and MMA of 1.0∶1.2, and a catalyst molality of 20 ×10-6 ~60 ×10 -6 at 70~80℃for 5 hours.The optimal conditions for the preparation of PDMS-MAAx were that 20%mass fraction of NaOH in NaOH solution, and the volume of the NaOH solution and ethanol was threefold and one time of the PDMS -MMAx .