Mechanism of Increasing A-Tig Welding Penetration

FY Liu,CL Yang,SB Lin,L Wu,QT Zhang

DOI: https://doi.org/10.3321/j.issn:0412-1961.2003.06.021

2003-01-01

Abstract:By using an 1 mm thick tungsten plate blocking the flow of molten metal, welding was performed on three specimens of 0Cr18Ni9 coated with active additions containing Bi, SiO2 and TiO2. The distributions of Bi after adding SiO2 and TiO2 at the both sides of the tungsten plate were measured, and the arc voltages are collected. The results show that additional SiO2 and TiO2 change the flow direction of the melting metal. Arc voltage increased 4.2 V due to adding SiO2, whereas no change occurs when adding TiO2. The active flux doesn't make the arc wholly constrict, but inflate. SiO2 leads to the constriction of plasma. Thus, the main reason Of SiO2 increasing arc voltage is plasma constriction and the increase in length of electrical path. Improvement of penetration by SiO2 is resulting from plasma constriction, anode spot constriction and the change of surface tension temperature coefficient instead of arc constriction. However, the mechanism improving penetration by TiO2 is only the change of surface tension temperature coefficient.