A Study on Directional Solidification of in Situ Cu 0 8cr Alloy

Peng Li

1999-01-01

Abstract:Directionally solidified procedure of the hypo eutectic alloy, Cu 0 8wt%Cr, under the status of non equilibrium solidification, was studied Results show that when the temperature gradient is 30℃/cm and the growth speed is 3μm/s and 30μm/s respectively, the microstructure of this alloy is a non stable one of α dendrite plus (α+β) eutectic; furthermore, the primary distance among α dendrites increases with the rise of the growth speed of dendrites This is in accordance with the varying rule of the primary dendritic distance within low speed period described by Hunt model, but contrary to that described by K F model Forming the Cr fibers depends on the surface tension of liquid Cr, the cross wise diffusion power of Cr atoms in liquid phase, and the growth environment for Cr phase between α dendrites So improving the diffusion of Cr, decreasing the lateral branch of α could help the formation of regular fibers of Cr