Highly efficient separation of titanium minerals from a modified bauxite residue through direct reduction: A comparison study
Yuguan Zhang,Yilin Wang,Lingyun Yi,Tiangui Qi,Qiusheng Zhou,Zhihong Peng,Guihua Liu,Xiaobin Li
DOI: https://doi.org/10.1016/j.jmrt.2023.09.017
IF: 6.267
2023-09-09
Journal of Materials Research and Technology
Abstract:Bauxite residue, which is a solid waste generated during the production of alumina, contains significant amounts of iron (Fe) and titanium (Ti) resources. The large-scale utilization of bauxite residue has become an urgent concern from both an environmental and resource perspective. In this study, a calculation of phase diagram (Calphad) was conducted to analyze the changes in mineral phases during the direct reduction process of both the current and reductive Bayer bauxite residue. Additionally, a comparison experiment was performed to investigate the enrichment and separation characteristics of iron and titanium minerals. The results indicated that during the carbon thermal reduction process, titanium existed as CaTiO 3 and Na-Al-Si-Ti molten phase slag in the current and reductive Bayer bauxite residue, respectively. Furthermore, NaFeO 2 was observed in the latter slag phase, which facilitated the migration and reduction of iron-containing minerals. The reductive Bayer bauxite residue was carbon thermal reduced for 1 hour at a temperature of 1200°C, with the addition of 7.5% Na 2 CO 3 . Following grinding and separation under a magnetic field strength of 0.08 Tesla, the iron grade of the concentrate, iron recovery, and TiO 2 grade in the tailing increased to 95.30%, 98.40%, and 50.50%, respectively. This was in comparison to the bauxite residue from current Bayer digestion, which showed values of 78.90%, 87.18%, and 14.87% under the same conditions. The findings of this work contribute to the potential utilization of iron and titanium present in bauxite residue from a modified Bayer digestion process.
materials science, multidisciplinary,metallurgy & metallurgical engineering