Abstract:The ruthenium catalyst supported on alumina was prepared by the method of incipient wetness impregnation. Ammonia synthesis over the catalyst was performed under the conditions; of 0 similar to 10 mpa, 425 or 475 degreesC, and space velocity of 20 000 h(-1) with synthesis gas of N-2-H-2, (1: 3). X-ray diffraction, nitrogen physical adsorption, and CO2 chemisorption were employed to characterize the phase, specific surface area, and surface basicity of alumina. With the increase of AI(OH)(3) calcination temperature from 600 to 900 degreesC, the surface basicity of alumina increased from 0.51 to 0.75 mmol/g, the specific surface area of alumina decreased from 223 to 140 m(2)/g. The calcination temperature of 800 degreesC gave the highest activity of Ba-Ru-K/Al2O3(39.38 mmol/(g(.) h) at 5 MPa and 475 degreesC). The presence of promoters K, Ba, and Sm increased significantly the activity of Ru/Al2O3, furthermore, promoters Ba, and Sm weakened the strong adsorption of hydrogen on the Ru sites, which increased greatly the activity of Ru/Al2O3 at high pressures. The surface basicity of alumina modified with MgO increased from 0.68 to 1.01 mmol/g, the specific surface area of alumina decreased from 168 to 72 m(2)/g, and the activity of Ba-Ru/Al2O3-MgO increased from 17.52 to 65.76 mmol/(g(.)h) (at 5 MPa and 475 V) when the mole content of MgO in alumina increased from 0 to 75 %. While the surface basicity, specific surface area of alumina modified with BaO, and the activity of Ru-K/Al2O3-BaO first increased and then decreased with the increase of the mole content of BaO in alumina from 0 to 33.3 %. When the mole content of BaO was equal to 7.7 %, the highest activity (34.47 mmol/g(.)h) at 5 MPa and 475 degreesC was obtained. If the mole content of BaO in alumina further increased, the specific surface area of alumina, and the activity of Ru-K/Al2O3-BaO would decrease dramatically because the Al2O3-BaO mixture oxide was present in the phase of BaAl2O3.

Interaction among Metal, Promoter and Support over Cesium/Active Carbon-Promoted Ruthenium-Based Catalyst for Ammonia Synthesis

Promoted Ru/PrOx Catalysts for Mild Ammonia Synthesis

Preparation of Carbon-Supported Ru-based Catalyst for Ammonia Synthesis

Enhanced Ammonia Synthesis Activity of Ceria-Supported Ruthenium Catalysts Induced by CO Activation

Study on Ruthenium Ammonia Synthesis Catalyst Supported on Carbon

Ruthenium Complex Hydride Catalyst as a Platform for Ammonia Synthesis: The Effect of Alkali or Alkaline Earth Elements

Electronic metal-support interaction enhanced ammonia decomposition efficiency of perovskite oxide supported ruthenium

Promoting Metal Oxides–zeolite Electron Interaction on MnCeOx/HY Catalyst for Boosting Nitrogen Oxides Reduction

Activity influence factors of ruthenium catalysts supported on MOx for ammonia synthesis

Study on Preparation Condition of Ru-Based Ammonia Synthesis Catalyst

Ru-Based Catalysts for Ammonia Decomposition: A Mini-Review

Strong metal‒support interaction modulates catalytic activity of Ru nanoparticles on Gd2O3 for efficient ammonia decomposition

KOH Activation of Thermally Modified Carbon as a Support of Ru Catalysts for Ammonia Synthesis

Tuning clusters-metal oxide promoters electronic interaction of Ru-based catalyst for ammonia synthesis under mild conditions

Effect of Ultrasonic Treatment of Activated Carbon Support on Catalytic Performance of Ru/Ac for Ammonia Synthesis

Ruthenium Supported on Cobalt‐Embedded Porous Carbon with Hollow Structure as Efficient Catalysts toward Ammonia‐Borane Hydrolysis for Hydrogen Production

Effects of Preparation Condition and Support Modification on Ammonia Synthesis over Alumina-Supported Ruthenium Catalyst

Engineering the Metal‐Support Interaction and Oxygen Vacancies on Ru@P‐Fe/Fe3O4 Nanorods for Synergetic Enhanced Electrocatalytic Nitrate‐to‐Ammonia Conversion

Effects of Using Carbon-Coated Alumina as Support for Ba-Promoted Ru Catalyst in Ammonia Synthesis

Regulating oxygen vacancies by Zn atom doping to anchor and disperse promoter Ba on MgO support to improve Ru-based catalysts activity for ammonia synthesis

Barium Oxynitride Electride as Highly Enhanced Promotor for Ruthenium Catalyst in Ammonia Synthesis: Comparative Study with Barium Oxide