Abstract:As the saying goes that “no ash, no glaze”, lime-ash has been the core material widely used to prepare glaze in ancient China. Among all the lime-ashes, those made in Jingdezhen are the most influential and representative ones. Not only did lime-ash contribute greatly to the prosperity of porcelain making of Jingdezhen in Song, Yuan, Ming and Qing Dynasty, but also it has a complicated, rigorous and a touch of “mysterious” in its preparation process, technical principle and glaze mechanism. Therefore, the research of the lime-ash has been an important subject in exploring the “secret” of ancient Chinese porcelain production by Chinese and foreign researchers. In this paper, four representative firewood and two lime stones as the raw materials were collected for the comparative studies, and three kinds of lime-ash with different smolder times were collected from one of the only two traditional lime-ash workshops in Shou’an town nearby Jingdezhen urban area. The chemical composition and phase composition of the raw materials and lime-ash with different smolder times made in Jingdezhen were discussed by testing with the Energy Dispersive X Ray Fluorescence (EDXRF) and X-Ray Diffraction (XRD). The results showed that Fe(2)O(3), MnO contents reaches 1.41% and 1.52% respectively, but the P(2)O(5) content is just 0.54% of Langqi grass which is lower than other firewood that is not only benefited to form the characteristic of “Green in the white” in Jingdezhen traditional glaze, but also is favor to enhance the transparency of glaze and promote the coloration of traditional under-glazed color painted porcelain, such as the blue and white porcelain. The CaO content of grey lime stone is lower than that of the black lime stone with MgO content of 35.79%.This could be the main reason why the craftsmen prefer to use black lime stone to prepare lime-ash. In addition, the EDXRF results show that the K(2)O, P(2)O(5), MnO and Fe(2)O(3) contents have increased as the time of smoldering increases. In the meanwhile, the calcium carbonate (CaCO(3)) phase has also increased, but the calcium hydroxide (Ca(OH)(2)) phase has decreased. The study helps Jingdezhen porcelain “look like jade” and is also good to avoid the “thickness” of glaze when there is a certain amount of Ca(OH)(2) in glaze. So it could be concluded that the unique raw materials and smolder technology of the lime-ash which have provided the technical support for the development of lime-ash glaze are the unique features of ancient Jingdezhen ash glaze.

AN APPROACH TO THE PROCESSING OF MnO-PbO-ZnO SYSTEM LUSTER GLAZE

Preparation of transparent glaze enhanced by mullite crystals with branched architecture

Synthesis and Coloring Mechanism of Metallic Glaze in R2O-RO-Al2O3-SiO2-P2O5 System

RESEARCH ON THE EFFECT OF STABILIZING AGENTS ON THE PERFORMANCES OF GREEN LEADLESS AND CADMIUMLESS FLUXING AGENTS FOR OVERGLAZE COLORS

Study on Environment-Fridenly Leadless Flux for Overglaze Colorswith Low Bismuth Content

Study on Leadless and Cadmiumless Fluxing Agent for Overglaze Colors

Research on the Preparation of Envionment-Protecting Leadless Fluxing Agent for Overglaze Colors with Low Bismuth

One‐step preparation of glass‐ceramics from a ferrochrome slag and an electrolytic manganese slag

Effect of W(mgo)/w(al2o3) Ratio and Basicity on Microstructure and Metallurgical Properties of Blast Furnace Slag

Effects of Fluxes and Coloring Aids on the Performances of Leadless and Cadmiumless Fluxing Agents for Overglaze Colors

Preparation of a highly color-saturated amorphous photonic crystal structural color glaze by imitating the multilayered structure of Jun porcelain

Existing state and solidification characteristics of heavy metals in glass‐ceramics from Mn‐bearing blast furnace slag

Effect of superheat degree and MnO on structural characteristics of CaO-SiO 2 -TiO 2 -based blast furnace slags

Effect of manganese on the structure of CMAS slag glass–ceramics

Formation mechanism of titania based opacified glaze with novel core-shell nanostructure

Effect of BaO and MnO on high-temperature properties and structure of blast furnace slag

Influence of Ca3(PO4)2 on the Surface Morphology and Properties of a CaO-Al2O3-SiO2-Fe2O3-Based High Temperature Phase Reconstructed Complex

RESEARCH ON PREPARATION OF SUPERFINE ALUMINA NANONPOWDER AND REINFORCED CELADON CERAMIC BODY

A study of the solidification and stability mechanisms of heavy metals in electrolytic manganese slag-based glass-ceramics

[Effect of Raw Materials and Preparing Process on the Composition of Lime-Ash]

RESEARCH ON THE EFFECT OF ALKALINE METAL OXIDES AND FLUORIDES ON THE PERFORMANCES OF GREEN LEADLESS FLUX FOR OVERGLAZE COLORS