Abstract:Micelles and hydrogels, generally prepared at different concentrations in waters, arouse great interest due to their wide application. However, it is inconvenient and difficult to prepare the micelles and hydrogels at the same concentrations. In this work, different states of a same copolymer, such as micelle solutions and hydrogels, are prepared via the polymerization of the pre-assembled acrylic acid and styrene with the same monomer compositions at the same concentrations. The influence of initiator (azodiisobutyronitrile) concentration on the structures of the aggregates is investigated, and the corresponding molecular structures of the copolymers are studied by nuclear magnetic resonance and dynamic thermomechanical analysis, whereas the morphology of the aggregates is characterized by scanning electron microscope and transmission electron microscope. As a supplement to the experiment, dissipative particle dynamics simulation is further performed to reveal the aggregate structures and the corresponding molecular structures of the copolymers. It is found that, under the same concentration of acrylic acid and styrene, the system with a higher initiator concentration (7.0 x 10(-3) mol/L) tend to form stable spherical micelles of 50 nm diameter, in which the copolymers have longer blocks; while that with a lower initiator concentrations (such as 7.0 x mol/L) tend to form network hydrogels, in which the copolymers have alternated and shorter blocks. Both the dynamic thermomechanical analysis and the simulation results demonstrate that the diblock copolymers and multiblock copolymers are synthesized at the higher and the lower initiator concentration. The different aggregate structures are originated from the different molecular structures. In addition, rheological characterization techniques are employed to investigate the rheological properties of the solutions and the hydrogels to clarify the relations between the properties and the molecular/aggregate structures. The rheological characterization showed the shear thinning non-Newtonian behaviour for both the micelle solutions and the hydrogels, and the gel-point of hydrogels was determined to be at the concentration of 22 wt%. It is found that the hydrogels are recoverable after destruction by large amplitude oscillatory shear. The work can serve as an example to clarify the role of the polymer microstructure in determining the material properties and to provide guides for constructing materials with the similar composition but different aggregate structure.

Study on Preparation of Transparent Microporous Polymer Gels from Microemulsion Polymerization

Polyurethane Acrylate Microgel Synthesized by Emulsion Polymerization Using Unsaturated Self-Emulsified Polymer

Preparation of Bicontinuous Porous Polymeric Materials Via Microemulsion Polymerization

Preparation of Acrylic Microgels by Modified Microemulsion Polymerization and Phase Inversion

Synthesis and Structure of the Poly(methyl Methacrylate) Microlatex

Preparation and Characterization of Poly (N-Isopropylacrylamide-co-dimethylaminoethyl Methacrylate) Microgel Latexes

Preparation and Thermal Response Behavior of Poly(n‐isopropylacrylamide‐co‐a Crylic Acid) Microgels Via Soap‐free Emulsion Polymerization Based on AIBN Initiator

Thermosensitive ionic microgels via surfactant-free emulsion copolymerization and in situ quaternization cross-linking.

Preparation of uniform microcapsules with silicone oil as continuous phase in a micro-dispersion process.

Preparation and properties of thermo-sensitive organic/inorganic hybrid microgels

Formation of Microporous Polymeric Materials by Microemulsion Radiation Polymerization of Butyl Acrylate

Radiation Preparation of Microporous Materials Using Bicontinuous Microemulsion Polymerization

Synthesis of Poly(N,N '-Methylenebisacrylamide-co-4-vinylpyridine) Microgels by Gamma-Ray Irradiation

Preparation of Thermo-Sensitive Polymer Microgels by Altered-Temperature Suspension Polymerization

Preparation of Micelles and Gels Via Polymerization of Pre-Assembled Styrene and Polyacrylic Acid

Electrochemical synthesis of polymer microgels

Preparation and Properties of Polyacrylic Acid Microgel by Precipitation Polymerization in Organic Solvent

Polymerization Of Butyl Acrylate In Anionic Microemulsion

Synthesis of poly( acrylic acid) nano- and microparticles using an inverse emulsion polymerization method

Synthesis and Properties of Organic-Inorganic Hybrid P(Nipam-Co-Am-Co-Tmspma) Microgels

PREPARATION AND PROPERTIES OF CLAY/POLY(N-ISOPROPYLACRYLAMIDE-co-ACRYL AMIDE)NANOCOMPOSITE HYDROGELS