Systhesis and Photoluminescence Character of SnO2 Nanobelts

张翔晖,王月娇,韩祥云,高义华,黄德修,张端明
IF: 17.694
2009-01-01
NanoScience and Technology
Abstract:SnO2 nanobelts with smooth surface and uniform size were fabricated by direct thermal evaporation of tin powders under atmosphere pressure.It is found that high-temperature annealing is effective to transform the mixed phases of Sn3O4 and SnO2 to the rutile phase of SnO2.The photoluminescence characteristics of SnO2 nanostructures were studied thoroughly.The results showed that there were two PL peaks,the stronger is around about 600 nm and the weaker ia around 375nm before annealing.After annealing,the peak at 375nm disappeared,which may be due to the decrease of lattice defects in the SnO2 nanobelts.