Pore Structure of Exfoliated Graphite and Its Varieties of Liquid Sorption

兆恒,周伟,曹乃珍,沈万慈,郑永平

DOI: https://doi.org/10.3969/j.issn.1673-2812.2002.02.001

2002-01-01

Materials Science and Engineering

Abstract:The pore structure of EG was measured by nitrogen adsorption and mercury porosimeter methods.The space around EG particle was observed by SEM and the porosity of EG was measured by pycnometer method.The results showed that the porosity of EG grains was more than 85%, the porosity of open pore and close pore in EG was more than 13% and less than 1%,respectively.\;The present work divides the pores of EG into 4 levels.At level 1,EG particle contains V\|type open pores with dimension about several hundreds micrometer; at level 2,the wellowleaf\|type pores are perpendicular to the axis of worm grain with dimension of a few micrometers,in which most of pores are open;at level 3, the pores with dimension from 0.1 to several μm on the surface of lamella is perpendicular to the axis of worm grain;and at level 4, the pores with nanometer scale is only measured by nitrogen adsorption method.The specific surface area of EG is less than 100m\+2/g.\;During liquid adsorption/absorption process,the pores of EG grains are deformed and grains are shattered by the surface tension between EG and liquid.Larger the absorption amount is,more remarkable the effect is.