Abstract:The physical and mechanical properties and structural condition of flexible graphite foils produced by processing natural graphite with nitric acid, hydrolysis, thermal expansion of graphite and subsequent rolling were studied. The processes of obtaining materials and changing their characteristics has been thoroughly described and demonstrated. The structural transformations of graphite in the manufacture of foils were studied by X-ray diffraction analysis (XRD) and transmission electron microscopy (TEM). A decrease in the average size of the coherent scattering regions (CSR) of nanocrystallites was revealed during the transition from natural graphite to thermally expanded graphite from 57.3 nm to 20.5 nm at a temperature of 900 °C. The rolling pressure ranged from 0.05 MPa to 72.5 MPa. The thickness of the flexible graphite foils varied from 0.11 mm to 0.75 mm, the density—from 0.70 to 1.75 g/cm3. It was shown that with an increase in density within these limits, the compressibility of the graphite foil decreased from 65% to 9%, the recoverability increased from 5% to 60%, and the resiliency decreased from 10% to 6%, which is explained by the structural features of nanocrystallites. The properties’ anisotropy of graphite foils was studied. The tensile strength increased with increasing density from 3.0 MPa (ρ = 0.7 g/cm3) to 14.0 MPa (ρ = 1.75 g/cm3) both in the rolling direction L and across T. At the same time, the anisotropy of physical and mechanical properties increased with an increase in density along L and T to 12% with absolute values of 14.0 MPa against 12.5 MPa at a thickness of 200 μm. Expressed anisotropy was observed along L and T when studying the misorientation angles of nanocrystallites: at ρ = 0.7 g/cm3, it was from 13.4° to 14.4° (up to 5% at the same thickness); at ρ = 1.3 g/cm3—from 11.0° to 12.8° (up to 7%); at ρ = 1.75 g/cm3—from 10.9° to 12.4° (up to 11%). It was found that in graphite foils, there was an increase in the coherent scattering regions in nanocrystallites with an increase in density from 24.8 nm to 49.6 nm. The observed effect can be explained by the coagulation of nanocrystallites by enhancing the Van der Waals interaction between the surface planes of coaxial nanocrystallites, which is accompanied by an increase in microstrains. The results obtained can help discover the mechanism of deformation of porous graphite foils. The obtained results can help discover the deformation mechanism of porous graphite foils. We assume that this will help predict the material behavior under industrial operating conditions of products based flexible graphite foils.

THE RELATIONSHIP BETWEEN MECHANICAL PROPERTIES AND MICROSTRUCTURE OF FLEXIBLE GRAPHITE

Fracture mechanism of flexible graphite sheets

Research on mechanical properties of composite grid structures

Molecular Simulation and Experimental Investigation of Thermal Conductivity of Flexible Graphite Film

Effect of graphite and its surface modification on thermal conductivity of silicone rubber

Mechanical properties of graphene nanobuds: A molecular dynamics study

Effect of pore structure on the thermophysical and frictional properties of high-density graphite

Intrinsic Mechanical Properties of Graphene Oxide Films: Strain Characterization and the Gripping Effects

The Influence of Machining Conditions on the Orientation of Nanocrystallites and Anisotropy of Physical and Mechanical Properties of Flexible Graphite Foils

Mechanical Properties of Hydrogen Functionalized Graphyne - A Molecular Dynamics Investigation

Characterization of the flexural behavior of a reactive graphitic nanofibers reinforced epoxy using a non-linear damage model

Unveiling the Thickness-Dependent Mechanical Properties of Graphene Papers by in Situ SEM Tension.

Anisotropic high thermal conductivity of flexible graphite sheets used for advanced thermal management materials

Microstructure and properties of graphite nanoflakes/Cu matrix composites fabricated by pressureless sintering and subsequent thermo-mechanical treatment

Microstructure graphitization evolution and multi-scale, multi-mechanism synergistic enhancement of ultra-high strength carbon-graphite materials

Research on the thickness effect and micro-fracture mechanism of graphite sheets with layered structures

STUDU ON THE STRUCTURE OF EXPANDED GRAPHITE

Mechanical Properties of Agraphite Gasket Sealing Interface

Microstructure and mechanical properties of carbon graphite composites reinforced by carbon nanofibers

In situ tensile fracturing of multilayer graphene nanosheets for their in-plane mechanical properties

Deformation behavior of graphite and its effect on microstructure and thermal properties of aluminum/graphite composites