Thermal Equations of State of Theα,β, Andωphases of Zirconium
Yusheng Zhao,Jianzhong Zhang,Cristian Pantea,Jiang Qian,Luke L. Daemen,Paulo A. Rigg,Robert S. Hixson,George T. Gray,Yunpeng Yang,Liping Wang,Yanbin Wang,Takeyuki Uchida
DOI: https://doi.org/10.1103/physrevb.71.184119
2005-01-01
Abstract:We have conducted synchrotron x-ray diffraction studies on high purity zirconium metal at pressures sPd up to 17 GPa and temperatures sTd up to 973 K. Unit cell volumesVd were derived from the refinements of x-ray diffraction data for thea, b, andv phases of zirconium and fitted to a Birch-Murnaghan equation of state with the pressure derivative of the bulk modulus, K08, fixed at 4.0. The derived thermoelastic parameters for a zirconium are isothermal bulk modulusK0=92s3d GPa, temperature derivative of bulk modulus s]K /]TdP=−2.3s8d310 GPa/K, volumetric thermal expansivity aT=a+bT with a=1.5s±0.8d310−5 K−1 and b=1.7s±1.4d310−8 K−2, and the pressure derivative of thermal expansion s]a /]PdT=−2.7s9d 310−6 GPa−1 K−1. For theb phase we obtained an isothermal bulk modulus of KT=66s3d GPa at 973 K and a unit-cell volume ofVs973 Kd=47.7s3d Å3 at ambient pressure. For the v zirconium we obtainedK0 =90s5d GPa. Within the experimental errors, the K0 values we determined for the a and v phases and volumetric thermal expansion for the a phase are in agreement with previous experimental results, whereas all other thermoelastic parameters represent the first determinations for the three crystalline phases of zirconium metal.