Microstructural Evolution of AZ61-10 At.%ti Composite Powders During Mechanical Milling

Huan Yu,Yu Sun,Lianxi Hu,Haiping Zhou,Zhipeng Wan

DOI: https://doi.org/10.1016/j.matdes.2016.05.014

IF: 9.417

2016-01-01

Materials & Design

Abstract:The nanocrystalline AZ61 containing 10at.%Ti composite powders were synthesized by mechanical milling. The results indicate that mechanical milling is available to prepare AZ61-10 at.%Ti composite powders with nanocrystalline Mg matrix, fine dispersed Ti particles and supersaturated solid solutions of Al and Ti in Mg matrix. The microstructure and morphology evolution of magnesium matrix and Ti particles were observed by SEM and TEM. Meanwhile the solid solubility and grain size evolution of Mg matrix were calculated by XRD, with the corresponding mechanism being analysed. Specifically, the Mg grain and the Ti particles were refined with the increasing milling time. The Mg grain was refined to approximately 58.2nm and the Ti particle size was reduced to around 558nm after 110h mechanical milling. From XRD results of the as-milled powders, the supersaturated solid solution of Ti and Al in Mg matrix were detected. Generally, the Al might be completely dissolved into the Mg matrix after 110h mechanical milling. Correspondingly, the solid solubility of Ti in Mg matrix was estimated to be 3.18at.%. The micro-hardness of as-milled composite powders increased with the increasing milling time. The micro-hardness could reach 120.42HV being 2.1-fold the micro-hardness of raw AZ61 alloy.