Abstract:To obtain a versatile formaldehyde oxidation material, simultaneously increasing the oxidative ability, recyclability and deactivation repellence (e.g., enduring the interference from moisture and aromatic compound omnipresent in indoor air) is of great significance. Herein, the above properties of α-MnO2 were synchronously updated via one step treatment in oxalic acid (H2C2O4), and an in-depth understanding of the surface properties-performance relationship was provided by systematic characterizations and designed experiments. Compared with the pristine sample, XPS, ESR, O2-TPD, CO-TPR and pyridine-IR reveal that H2C2O4 created substantial Mn3+ species on surface, exposing a higher coverage of oxygen vacancies that actively participated in the dissociative activation of gas-phase O2 into reactive chemically adsorbed oxygen (OC), and the abundant Lewis acid sites further enabled the effective O2 activation process. The large amount of oxygen OC promoted the HCHO-to-CO2 conversion and inhibited the accumulation of formate that required a high temperature of 170 °C to be eliminated, thus conspicuously improving the α-MnO2's thermal recovery. The combined H2O-TPD, H2O-preadsorbed CO-TPR, C6H6-TPD and C6H6-preadsorbed CO-TPR investigations shed light on the H2C2O4-induced water and benzene resistance. The notably weakened water and benzene binding strength with the H2C2O4-modified surface together with the unrestrained oxygen OC accounted for the outstanding anti-deactivation performance.

Room-Temperature Oxidation of Formaldehyde by Layered Manganese Oxide: Effect of Water

Catalytic Ozonation of Formaldehyde with an Oxygen-Vacancy-Rich MnOx/γ-Al2O3 Catalyst at Room Temperature

Control over the Morphology and Structure of Manganese Oxide by Tuning Reaction Conditions and Catalytic Performance for Formaldehyde Oxidation

The Effect of Manganese Vacancy in Birnessite-Type MnO2 on Room-Temperature Oxidation of Formaldehyde in Air

Novel synergistically effects of palladium-iron bimetal and manganese carbonate carrier for catalytic oxidation of formaldehyde at room temperature

Study of manganese–cerium composite oxide catalysed oxidation for low concentration formaldehyde at room temperature

Enhanced oxidative ability, recyclability, water tolerance and aromatic resistance of α-MnO2 catalyst for room-temperature formaldehyde oxidation via simple oxalic acid treatment

Low-Temperature Oxidation Removal of Formaldehyde Catalyzed by Mn-Containing Mixed-Oxide-Supported Bismuth Oxychloride in Air

Degradation of Low Concentration Formaldehyde by Mesoporous MnO2 at Room Temperature

Formaldehyde oxidation at room temperature over layered MnO2

The catalytic efficacy of modified manganese-cobalt oxides for room-temperature oxidation of formaldehyde in air

Layered manganese oxides for formaldehyde-oxidation at room temperature: the effect of interlayer cations

Room temperature oxidation of gaseous formaldehyde over silver-doped manganese oxide catalyst

Insights into the effect of superficial lattice oxygen in formaldehyde oxidation on birnessite

Synthesis and Catalytic Performance of Manganese Oxide Octahedral Molecular Sieve Nanorods for Formaldehyde Oxidation at Low Temperature

MnOx–CeO2 Mixed Oxide Catalysts for Complete Oxidation of Formaldehyde: Effect of Preparation Method and Calcination Temperature

Simultaneously Catalytic Decomposition of Formaldehyde and Ozone over Manganese Cerium Oxides at Room Temperature: Promotional Effect of Relative Humidity on the MnCeOx Solid Solution

Study on the Formaldehyde Oxidation Reaction of Acid-Treated Manganese Dioxide Nanorod Catalysts

Potassium-modulated Δ-Mno2 As Robust Catalysts for Formaldehyde Oxidation at Room Temperature

Enhanced Formaldehyde Oxidation of Plywood Using MnO2 Nanoflowers Supported on Porous Hydrothermal Carbon at Ambient Temperature

Deactivation of Layered MnO2 Catalyst During Room Temperature Formaldehyde Degradation and Its Thermal Regeneration Mechanism