Rietveld Refinement, Microstructure and Ferromagnetic Resonance Linewidth of Iron-Deficiency NiCuZn Ferrites

Ke Sun,Zhiyong Pu,Yan Yang,Linglong Chen,Zhong Yu,Chuanjian Wu,Xiaona Jiang,Zhongwen Lan

DOI: https://doi.org/10.1016/j.jallcom.2016.04.164

IF: 6.2

2016-01-01

Journal of Alloys and Compounds

Abstract:Ni0.56+x/2Zn0.34Cu0.1Fe2.0-xO4-x (x = 0, 0.02, 0.04, 0.06, 0.08, 0.12) ferrites have been prepared by the solid-state reaction method. The Rietveld refinement of X-ray diffraction patterns, microstructure, static magnetic properties and ferromagnetic resonance (FMR) linewidth of NiCuZn ferrites have been analyzed by X-ray diffraction, scanning electron microscopy (SEM), B-H analyzer and electron spin resonance (ESR) spectrometer, respectively. The FMR linewidth was investigated by an approximate calculation based on spin wave approach. The results revealed that all the samples were a single NiCuZn spinel phase. With the increase of iron-deficient amount, the lattice parameter (a) displayed a decreasing trend. However, the bulk density first increased rapidly and then trended to go up slightly. The saturation magnetization of stoichiometric NiCuZn ferrites was much lower than that of iron-deficient samples. This phenomenon is ascribed to the combined effect between molecule magnetic moment and bulk density. The magnetocrystalline anisotropy constant, derived from the law of approach to saturation, has been discussed. The anisotropy and porosity linewidth broadening models were adopted to identify the linewidth contribution. The results manifested that the porosity linewidth broadening was much larger than the anisotropy linewidth broadening. (C) 2016 Elsevier B.V. All rights reserved.