Synthesis of a full range Fe-doped ZnFexCo2-xO4 and its application as anode material for lithium-ion battery.
You Wu,Jun Zhang,H. Duan,Yanming Zhao,Youzhong Dong
DOI: https://doi.org/10.1039/d1dt02865k
IF: 4
2021-10-05
Dalton Transactions
Abstract:Fe-Doped ZnFexCo2-xO4 (x = 0.00, 0.17, 0.33, 0.47, 0.67, 0.87, 1.17, 1.37, 1.67, 1.87, 2.00) compounds were prepared by a sol-gel method. X-ray diffraction measurements show that Fe-doping does not change the crystal structure of ZnCo2O4 and dopant Fe successfully occupies the 16c Co site. Because of the bigger radius of the doping ion, the cell parameters and cell volumes of ZnFexCo2-xO4 compounds present an obvious linear increase with increasing Fe content. In addition, attributed to the similar crystal structures for ZnFe2O4 and ZnCo2O4, a full range (0 ≤ x ≤ 2) of ZnFexCo2-xO4 solid solution phases was obtained. V/I measurement results show that a small Fe doping content obviously improved the electronic conductivity of the sample. In addition, due to the smaller particles size and uniform particle distribution caused by Fe doping, the lithium ion diffusion coefficient of the sample was increased by 2 orders of magnitude. Based on the improved electronic conductivity combined with the significantly increased lithium-ion diffusion coefficient, a sample with Fe doping content of x = 0.33, ZnFe0.33Co1.67O4, presents a high reversible specific capacity and excellent rate cycle stability. At a rate of 100 mA g-1, a relatively high discharge capacity of 850 mA h g-1 can still be obtained after 100 cycles, which is obviously higher than that of pure ZnCo2O4 (only 295 mA h g-1). Even at a higher discharge rate of 500 mA g-1, a discharge capacity of 450 mA h g-1 with a capacity retention of nearly 100% was obtained. Based on its excellent electrochemical properties, ZnFe0.33Co1.67O4 will be a promising anode material for rechargeable lithium-ion batteries.
Medicine