Abstract:Linear fluorinated poly(arylene ether)s with and without pendent allyl groups (CFPAE and FPAE) were successfully polymerized from decafluorobiphenyl at room temperature. The subsequent SN2 nucleophilic substitution of the remaining F atom on CFPAE and FPAE with sodium 4-hydroxybenzenesulfonate yielded SCFPAE and SFPAEs in one simple step under mild conditions. The chemical structures of the polymers were confirmed by H-1 NMR and FT-IR. The ion exchange capacity (IEC), inherent viscosity, water uptake, swelling ratio, proton conductivity, mechanical property, thermal stability, and oxidative stability of the SFPAEs were characterized. The experimental results revealed that the IEC of the SFPAEs can be facilely controlled by the loading amount of sodium 4-hydroxybenzenesulfonate in the reaction mixture. The SFPAE-20 with an IEC of 2.0 mmol g(-1) exhibited an in-plane proton conductivity of 106 mS cm(-1) at 30 degrees C, higher than that of Nafion N212. More importantly, the SFPAEs showed significantly enhanced oxidative stabilities compared to sulfonated non-fluorinated analogs in literature. While there was still a trade-off between proton conductivity and mechanical strength as often seen for homogeneous systems, the SFPAEs were demonstrated to be promising candidates for proton exchange membranes. (C) 2017 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.

Poly(Tetrafluoroethylene-Cio-Perfluorovinyl Ether Sulfonamide) For Anion Exchange Membranes

Facile Preparation of an Ether-Free Anion Exchange Membrane with Pendant Cyclic Quaternary Ammonium Groups

Synthesis of Perfluorinated Ionomers and Their Anion Exchange Membranes

A Cross-Linked Fluorinated Poly (aryl Ether Oxadiazole) S Using a Thermal Cross-Linking for Anion Exchange Membranes

Synthesis of Novel Branched Fluorinated Poly(aryl Ether Oxadiazole)s for Anion Exchange Membranes

Poly(arylene Ether)s with Pendant Sulfoalkoxy Groups Prepared by Direct Copolymerization Method for Proton Exchange Membranes

Facile Synthesis of Fluorinated Poly(arylene Ether)s with Pendant Sulfonic Acid Groups for Proton Exchange Membranes

Synthesis and Characterization of A Fluorinated Cross-Linked Anion Exchange Membrane

Synthesis and Properties of Poly (aryl Ether Sulfones) Functionalized with Pendant Perfluoroalkyl Sulfonic Acid for Proton Exchange Membrane

Preparation and Characterization of Fluorinated Poly(aryl Ether Oxadiazole)s Anion Exchange Membranes Based on Imidazolium Salts

Preparation and Properties of Proton Exchange Membranes Based on Side-Chain Type Fluorinated Sulfonated Poly (aryl Ether) S

Phenyltrimethylammonium Functionalized Polysulfone Anion Exchange Membranes

A stable anion exchange membrane based on imidazolium salt for alkaline fuel cell

Synthesis And Characterization Of Perfluoroalkyl Sulfonic Acid Functionalized Polyphosphazene For Proton-Conducting Membranes

Perfluorosulfonated Ionomers Membranes: Melt-Processing And Characterization For Ion Exchange Applications

Synthesis and characterization of ion exchange capacity controlled and self-crosslinked anion exchange membranes

Partially Fluorinated Poly(arylene Ether)s Bearing Long Alkyl Sulfonate Side Chains for Stable and Highly Conductive Proton Exchange Membranes

Synthesis and Characterization of Sulfonated Poly(Arylene Ether Phosphine Oxide)S with Fluorenyl Groups by Direct Polymerization for Proton Exchange Membranes

Synthesis And Properties Of Sulfonated Poly(Phthalazinone Ether Phosphine Oxide)S With Perfluorobiphenyl Moieties For Proton Exchange Membranes

Low Water Swelling and High Proton Conducting Sulfonated Poly(arylene Ether) with Pendant Sulfoalkyl Groups for Proton Exchange Membranes