Preparation and Properties of Filling-type Sulfonated Poly (arylene ether sulfone)/Poly (ether sulfone) Composite Membranes with Microporous Structures
Zhu Yuxin,Alphonse Haragirimana,Lu Yao,Ingabire Providence Buregeya,Ning Cong,Li Na,Hu Zhaoxia,Chen Shouwen
DOI: https://doi.org/10.7503/cjcu20180785
2019-01-01
Abstract:A series of filling-type composite polymer exchange membranes was prepared based on sufonated poly (arylene ether sulfkmes) (SPAES) and poly ( ether sulfkme) s(PES) , and the properties including water uptake, dimensional change, thermal-mechanical properties , proton conductivity , methanol permeability and chemical stability were evaluated. Firstly, a series of microporous composite proton exchange membranes (Sx-y, x refers to the sulfonation degree of the SPAES copolymers, y refers to the mass ratio (20%-40%) of SPAES copolymers) was fabricated via immersion phase inversion method from PES and SPAES copolymers with suffimation degree of 30% (S30) , 40% (S40 ) and 50% (S50). Then, the corresponding filling-type composite polymer exchange membranes( Sx-y+F50) were prepared by filling S50 in the Sx-y micropores by vacuum filtration. The results indicate that the Sx-y membranes, despite of the rather low ion exchange capacity (IEC) , all display fairly high proton conductivity , fine mechanical strength, excellent chemical stability and rather low methanol permeability. After filling with S50, the corresponding Sx-y+F50 membranes exhibit improved IEC and proton conductivity , lowered methanol permeability , and maintain high mechanical strength and chemical stability. The S30-40+F50 membrane(IEC = 0. 69 mmol/g) shows the best comprehensive properties : proton conductivity of 50. 4 mS/cm at 90 degrees C in water; mass loss of 8. 2% and proton conductivity loss of 9% by aging in water at 140 degrees C for 24 h , and mass loss of 0. 66% by soaking in Fenton reagent( 3% H2O2, 20 mg/L FeSO4) at 80 degrees C for 1 h; methanol permeability of 6. 8x10(-8) cm(2)/s. The filling-type composite proton exchange membranes are promising candidates for fuel cell applications.