pH-responsive poly(ether sulfone) composite membranes blended with amphiphilic polystyrene-block-poly(acrylic acid) copolymers
Tao Luo,Shuo Lin,Rui Xie,Xiao-Jie Ju,Zhuang Liu,Wei Wang,Chuan-Lin Mou,Changsheng Zhao,Qianming Chen,Liang-Yin Chu
DOI: https://doi.org/10.1016/j.memsci.2013.09.002
IF: 9.5
2014-01-01
Journal of Membrane Science
Abstract:pH-responsive poly(ether sulfone) (PES) composite membranes blended with amphiphilic polystyrene-block-poly(acrylic acid) (PS-b-PAA) diblock copolymers are fabricated through simple phase inversion in water. The anchor block PS has a lower surface tension than that of PES, which is beneficial to anchor the PS block near the membrane pore surfaces. Modification of membrane matrix surface including membrane surface and pore surface by PAA chains is achieved by surface-segregation of PS-b-PAA copolymers, and confirmed by water contact angle measurement on membrane surface and confocal laser scanning microscopy characterization of membrane cross-section. The effects of the blended PS-b-PAA copolymers on the microstructures and pH-responsive characteristics of the PES composite membranes are investigated systematically. The hydraulic permeation results show that the pH-responsive characteristics of composite membranes blended with PS-b-PAA copolymers are proven to be significant, fast, reversible and durable with pH switching between 3 and 8. FITC-dextran sieving experiments of a PS-b-PAA blended composite membrane at ambient pH values of 3 and 8 show 28% and 90% rejection of 70kDa solute, respectively. At pH=3 (<pKa), the membrane pores are in “open” state because of the shrunken conformation of the PAA chains on the pore surfaces; in contrast, at pH=8 (>pKa), the membrane pores are in “closed” state due to the swollen conformation of the PAA chains. The results provide valuable guidance for fabricating stimuli-responsive membranes by blending amphiphilic block copolymers.