Synthesis and Luminescence Properties of (la,ce,tb)bo_3 Phosphors
王林生,文小强,周健,赖华生,王玉香,黄可龙
2009-01-01
Abstract:The phosphor of (La,Ce,Tb)BO3 was synthesized by high temperature solid state reaction. X-ray diffraction(XRD) patterns indicated that (La,Ce,Tb)BO3 and LaBO3 have the same crystal structure, the crystal structure was not changed by doping with Ce3+ and Tb3+. Emission scanning electron microscopy (SEM) image showed that the phosphor particles is uniform, the morphology is regular, and the granularity is about 5 μm. The luminescence properties of (La,Ce,Tb)BO3 phosphor were studied, both the Tb3+ characteristic emission and excitation peaks and the Ce3+ characteristic emission and excitation peaks were observed in the emission and excitation spectrum of (La,Ce,Tb)BO3. The emission spectra of Ce3+ in (La,Ce)BO3 and the excitation spectra of Tb3+ in (La,Tb)BO3 have large superposition at 330~400 nm regions, which supply good conditions for energy transfer from Ce3+ to Tb3+. The energy transfer between Ce3+ and Tb3+ is primarily as resonance transfer. Both of (La,Ce,Tb)BO3 phosphor and commercial phosphor (La,Ce,Tb)-PO4 have main emission peak at 541 nm. Comparing (La,Ce,Tb)BO3 phosphor with commercial phosphor (La,Ce,Tb)BO3, (La,Ce,Tb)BO3 phosphor has a little red shift at 489 nm and its relative emission intensity was 94.7% of the commereial phosphor (La,Ce,Tb)PO4. Therefore, it is expected that (La,Ce,Tb)BO3 phosphor would be a promising green-emitting phosphors.