Microstructure and Strengthening Mechanisms in an Fcc Structured Single-Phase Nanocrystalline Co25ni25fe25al7.5cu17.5 High-Entropy Alloy

Zhiqiang Fu,Weiping Chen,Haiming Wen,Dalong Zhang,Zhen Chen,Baolong Zheng,Yizhang Zhou,Enrique J. Lavernia
DOI: https://doi.org/10.1016/j.actamat.2016.01.050
IF: 9.4
2016-01-01
Acta Materialia
Abstract:We report on a study of the design, phase formation, microstructure, mechanical behavior and strengthening mechanisms of a novel single-phase Co25Ni25Fe25Al7.5Cu17.5 (at.%) high-entropy alloy (HEA). In this investigation, a bulk nanocrystalline (nc) Co25Ni25Fe25Al7.5Cu17.5 HEA with the face-centered cubic (FCC) crystal structure was fabricated by mechanical alloying (MA) followed by consolidation via spark plasma sintering (SPS). The X-ray diffraction (XRD) and transmission electron microscopy (TEM) results revealed that a single FCC solid-solution phase with an average grain diameter of 24 nm was produced following MA. Following SPS, bulk samples exhibiting a bimodal microstructure with both nanoscale grains and ultra-fine grains (UFGs) and with an average grain diameter of 95 nm were obtained, possessing a single FCC solid-solution phase identical to that in the milled powders. The single-phase feature of the Co25Ni25Fe25Al7.5Cu17.5 HEA principally resulted from remarkably high mutual solubility in most binary atom-pairs of the constituent elements, which appears to correspond to a high entropy of mixing. Approximately 5 vol.% of nanoscale twins were observed in the bulk nc samples. The bulk nc Co25Ni25Fe25Al7.5Cu17.5 HEA exhibits a compressive yield strength of 1795 MPa with a hardness of 454 Hv, which is dramatically higher than the yield strength of most previously reported FCC structured HEAs (-130-700 MPa). Compared to those of the bulk coarse-grained (CG) Co25Ni25Fe25Al7.5Cu17.5 HEA fabricated by arc-melting, the yield strength and Vickers hardness values of the bulk nc samples increased by 834.9% and 251.9%, respectively. Quantitative calculations of the respective contributions from each strengthening mechanism demonstrate that grain boundary strengthening and dislocation strengthening are principally responsible for the measured ultra-high strength of the bulk nc Co25Ni25Fe25Al7.5Cu17.5 HEA. (C) 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
What problem does this paper attempt to address?