Abstract:Inclusions are prevalent in both natural and synthetic materials. Gaining a comprehensive understanding of their dynamic response and interaction with the surrounding matrix is essential in fundamental mechanics and engineering applications. This study aims to achieve such understanding through theoretical analysis, experimental investigations, and numerical simulations, focusing on the dynamic destruction of inclusions and the underlying mechanisms. Firstly, the circumferential, radial, and shear stresses around elastic heterogeneous inclusions were derived by the wave function expansion and Duhamel integration methods. Subsequently, a set of experiments on sandstone specimens containing three types of inclusions (plaster, epoxy resin, cement) were conducted utilizing the Split Hopkinson Pressure Bar (SHPB) system in conjunction with high-speed photography and Digital Image Correlation (DIC) techniques to obtain the surface deformation of inclusion specimens. Eventually, a series of Finite Element Method (FEM) numerical simulations adopted suitable materials were also carried out to investigate the fracture process of inclusion and matrix under dynamic impact. The results demonstrate that the stress distributions and fracture mode of matrix and inclusion are highly dependent on the physical and mechanical properties of the inclusions and the surrounding matrix, specifically, density ρ , elastic modulus E , Poisson's ratio v , and strength. With an increase in the E and v , there is a reduction in the concentration of circumferential stress, while the radial and shear stresses experience an increase. The experimental and numerical results corroborated the theoretical findings and indicated that the localized dynamic stress concentrations induced by wave scattering around the inclusions directly dominated both local and overall specimen failure. Due to the dissimilarities in elastic parameters and strength between the inclusion and the matrix, the stress state of the inclusion and the interface is not homogeneous. Under dynamic loading, the weaker inclusion experiences tensile cracking at both ends of the loading, and as the mechanical properties ( ρ, E, v , and strength) of the inclusion rise, a transition from tensile- hybrid-shear failure occurs within the inclusion. The findings of this study help us understand the dynamic failure mechanisms of dissimilar inclusions in brittle material.

Photoelastic Investigation of Interaction Between Matrix Crack and Different Shapes of Inclusions

Experimental study on the matrix crack-fiber interaction using photoelasticity method

Study on the Effect of Inclusion Shape on Crack-Inclusion Interaction Using Digital Gradient Sensing Method

Study on Crack-Inclusion Interaction Using Digital Gradient Sensing Method

Interaction between rectangular cracks embedded in infinite medium

Crack–inclusion interaction in a quasicrystal medium with nonlocal effect

Instrumented indentation measurements of residual stresses around a crack tip under single tensile overloads

Stress concentration near stiff inclusions: Validation of rigid inclusion model and boundary layers by means of photoelasticity

Mechanical Response and Failure Mechanism of Circular Inclusion Embedded in Brittle Materials under Dynamic Impact

Investigation of Dynamic Mode I Matrix Crack-Fiber Bundle Interaction in Composites Using Caustics

Investigation of Stress Intensity Factors for an Interface Crack in Multi-Interface Materials Using an Interaction Integral Method

Tuning Crack-Inclusion Interaction with an Applied T-stress

Quantitative characterization of the fracture behavior of sandstone with inclusions: Experimental and numerical investigation

Tuning crack-inclusion interaction with an applied T\documentclass[12pt]{minimal} \usepackage{amsmath} \usepackage{wasysym} \usepackage{amsfonts} \usepackage{amssymb} \usepackage{amsbsy} \usepackage{mathrsfs} \usepackage{upgreek} \setlength{\oddsidemargin}{-69pt} \begin{document}$$\varvec{T}$$\end{d

Mechanical and Fracture Behaviors of Brittle Material with a Circular Inclusion: Insight from Infilling Composition

2-D Mesoscopic Simulation of Two-Phase Materials Containing Microinclusions.

Experimental Study of Deformation Field Around the Matrix Crack Induced by Fiber Bundles Using DGS Method

Experimental Study on Stress Intensity Factor for an Axial Crack in a PMMA Cylindrical Shell

Interaction of newly defined stress intensity factors for angular corners in a row of diamond-shaped inclusions

Mechanical and cracking behavior of granite specimens containing various inclusions

Caustic analysis of stress singularities in orthotropic composite materials with mode-I crack