Abstract:This paper presents the experimental methods and findings in obtaining the strain behavior of mortar during freezing and thawing cycles (FTC) at the meso-scale under fully saturated condition and the coefficient of thermal expansion (CTE) and elastic modulus of mortar after FTC tests. A heat-cool cycle test comparing an oven-dried and undried mortar was also performed prior to the FTC test, confirming that oven drying at 105 degrees C does not affect the CTE of samples, thereby ensuring the reliability of the results. During FTC with constant moisture content, a limitation in the increase in tensile strain was observed and this tensile strain decreased until contraction was observed. The contraction is attributed to the removal of gel pore water arising from negative pressures. Due primarily to the absence of available water supply, the displaced pore water cannot be refilled, which results in contraction at the end of the FTC. More importantly, the results show that after FTC, the CTE of frost damaged mortar increases while its elastic modulus decreases, primarily owing to microcracking when frost damage sets in. Microcracks act as broken bridges that can detach the aggregate from the hardened cement paste and in effect reduces the thermal restraints that each part (fine aggregate and cement paste) exerts on the other. The hardened cement paste can then expand/contract more freely under temperature variation, and thus can significantly affect (increase) the CTE of the whole composite (mortar). Further, stress transfer in the material is prevented due to microcracking resulting in elastic modulus reduction.

Estimation of Ice Content in Mortar Based on Electrical Measurements under Freeze-Thaw Cycle

Theoretical Model for Estimation of Ice Content of Concrete by Using Electrical Measurements

Estimation of Ice Formation in Mortar Saturated with Sodium Chloride Solutions

Experimental Examination of Electrical Characteristics for Portland Cement Mortar Frost Damage Evaluation

Electrical Response of Mortar Saturated with NaCl Solutions under Freeze–Thaw Cycles

Change of the Coefficient of Thermal Expansion of Mortar Due to Damage by Freeze Thaw Cycles

RBSM-based Mesoscale Study of Frost Deterioration for Recycled Concrete Considering Air-Entrainment in Old and New Mortar

Meso-scale mechanical model for mortar deformation under freeze thaw cycles

Modeling and Mesoscale Simulation of Ice-Strengthened Mechanical Properties of Concrete at Low Temperatures

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

A Mathematical Model for the Electrical Resistivity of Cement Paste at Early Ages Considering the Partially Saturated State

Effect of moisture content on freeze–thaw behavior of cement paste by electrical resistance measurements

Experimental Investigation of the Deformational Behavior of the Interfacial Transition Zone (itz) in Concrete During Freezing and Thawing Cycles

Determining Porosity and Pore Network Connectivity of Cement-Based Materials by a Modified Non-Contact Electrical Resistivity Measurement: Experiment and Theory

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Mesoscale Simulation of Deformation for Mortar and Concrete under Cyclic Freezing and Thawing Stress

Experimental investigation on electrical response and mechanical performance of cementitious materials at low temperatures

Two‐dimensional Rigid Body Spring Method Based Micro‐mesoscale Study of Mechanical Strengthening/damaging Effects to Concrete by Frost Action

Prediction of Effective Chloride Diffusivity of Cement Paste and Mortar from Microstructural Features

Chloride Ingress Profiles and Binding Capacity of Mortar in Cyclic Drying-Wetting Salt Fog Environments