Abstract:Low-temperature CO oxidation over a compositional series of Pd-Au nanoalloy catalysts supported on silica fume was studied. Except for the pure metals, these materials invariably showed biphasic separation into palladium- and gold-rich components. Performance was optimal for a catalyst of bulk composition Pd(4)Au(1), a mixture of Pd(90)Au(10) (72.5 at. %) and Pd(31)Au(69) (27.5 at. %), that was remarkably active at 300 K and more stable than a pure Au catalyst. For bulk materials dominated by Pd (Pd:Au = 16:1; 8:1; 4:1), the palladium-rich alloy fraction frequently adopted hollow sphere or annular morphology, while the gold-rich crystals were often multiply twinned. Quantitative powder X-ray diffraction (XRD) showed that under the synthesis conditions used, the Au solubility limit in Pd crystals was approximately 12 at. %, while Pd was more soluble in Au (approximately 31 at. %). This was consistent with X-ray photoelectron spectroscopy (XPS), which revealed that the surfaces of Pd-rich alloys were enriched in gold relative to the bulk composition. In situ Fourier transform infrared spectra collected during CO oxidation contained a new band at 2114 cm(-1) (attributed to linear CO-Au/Au-Pd bonds) and reduced intensity of a band at 2090 cm(-1) (arising from a linear CO-Pd bond) with escalating Au content, indicating that the Pd sites became increasingly obscured by Au. High-resolution electron micrographs (HRTEM) of the Pd-rich alloys revealed atomic scale surface defects consistent with this interpretation. These results demonstrate that gold-containing biphasic Pd nanoalloys may be highly durable alternatives for a range of catalytic reactions.

Au/LaPO4 Nanowires: Synthesis, Characterization, and Catalytic CO Oxidation

Gold Nanoparticles on Electroless-Deposition-derived MnOx/C: Synthesis, Characterization, and Catalytic CO Oxidation

Au/PO43−/TiO2 and PO43−/Au/TiO2 Catalysts for CO Oxidation: Effect of Synthesis Details on Catalytic Performance

Cerium Phosphate-Supported Au Catalysts for CO Oxidation

Highly Efficient Nano-octahedral Au/γ-Fe2O3 Catalyst Synthesized by Dealloying Combined with Calcination for Low-Temperature CO Oxidation

Highly active and sintering-resistant heteroepitaxy of Au nanoparticles on ZnO nanowires for CO oxidation ☆

Metal Phosphates As a New Class of Supports for Gold Nanocatalysts

Highly Active Cofe Alloy Nanoparticlesencapsulated in N-Doped Carbon Nanostructures for Oxygen Reduction Reaction in Both Alkaline and Acidic Media

Gold Nanoparticles Supported on Hydroxylapatite As High Performance Catalysts for Low Temperature CO Oxidation

Au/LaVO 4 Nanocomposite: Preparation, characterization, and catalytic activity for CO oxidation

Gold Nanoparticles Deposited on Manganese(iii) Oxide As Novel Efficient Catalyst for Low Temperature CO Oxidation

Co Oxidation on Au/Fepo4 Catalyst: Reaction Pathways and Nature of Au Sites

Large-scale Synthesis and Catalytic Activity of Nanoporous Cu–O System Towards CO Oxidation

Biphasic Pd-Au Alloy Catalyst for Low-Temperature Co Oxidation

Transition Metal (fe2o3, Co3O4 and NiO)-Promoted CuO-Based Α-Mno2 Nanowire Catalysts for Low-Temperature CO Oxidation

Restructuring of 4H Phase Au Nanowires and Its Catalytic Behavior Toward CO Electro-Oxidation

Gold Nanoparticles on Fe-doped Co3O4 for Enhanced Low-Temperature CO Oxidation

Nanoporous CuO Ribbons Modified by Au Nanoparticles Through Chemical Dealloying and Calcination for CO Oxidation

Au@ZIF-8: CO oxidation over gold nanoparticles deposited to metal-organic framework.

Carbon nanotubes-templated assembly of LaCoO3 nanowires at low temperatures and its excellent catalytic properties for CO oxidation

Improved Catalytic Performance of Au/α-Fe2O3-Like-Worm Catalyst for Low Temperature CO Oxidation