Abstract:The present work highlights the versatility of a TiO 2 -Al 2 O 3 mixed oxide bearing highly dispersed gold nanoparticles that was applied in the CO oxidation reaction at room temperature. The TiO 2 , Al 2 O 3 , and TiO 2 -Al 2 O 3 supports were synthesized by the sol–gel method, while gold nanoparticles were added by the deposition–precipitation with urea method using a theoretical Au loading of 2 wt.%. A promotional effect of the TiO 2 -Al 2 O 3 support on the activity of gold catalysts with respect to TiO 2 and Al 2 O 3 was observed; Au/TiO 2 -Al 2 O 3 showed outstanding CO oxidation, being active from 0 °C and stable throughout a 24-h test. As for the alumina content (5, 10, and 15 wt.%) in TiO 2 , it improved the textural properties by retarding the crystal growth and anatase–rutile phase transformation of TiO 2 , suppressing the deposition of carbon on the catalyst surface and stabilizing the Au nanoparticles even at high temperatures. Gold was highly dispersed with nanoparticle sizes ranging from 1 to 2 nm when H 2 was used to treat thermally the Au/TiO 2 -Al 2 O 3 , Au/TiO 2, and Au/Al 2 O 3 materials. In addition, the XPS technique helped elicit that Au 0 and Au 1+ boosted their interaction with the TiO 2 , Al 2 O 3 , and TiO 2 -Al 2 O 3 supports by means of charge transfer, which resulted in outstanding CO oxidation activity from 0 °C. Likewise, the key factors that control the peculiar catalytic performance in the CO oxidation reaction are discussed, which represents a step forward in the versatility behavior of gold catalysts supported on mixed oxide catalysts.

Gold nanoparticles supported on manganese oxides for low-temperature CO oxidation

Gold Nanoparticles Deposited on Manganese(iii) Oxide As Novel Efficient Catalyst for Low Temperature CO Oxidation

Gold Nanoparticles on Electroless-Deposition-derived MnOx/C: Synthesis, Characterization, and Catalytic CO Oxidation

Catalytic behavior of gold nanoparticles supported on a TiO2-Al2O3 mixed oxide for CO oxidation at low temperature

Low Temperature Co Oxidation Over Unsupported Nanoporous Gold

Low Temperature CO Oxidation Over Highly Active Gold Nanoparticles Supported on Reduced Graphene Oxide@Mg-BTC Nanocomposite

Improved Catalytic Performance of Au/α-Fe2O3-Like-Worm Catalyst for Low Temperature CO Oxidation

Gold Nanoparticles Supported on Hydroxylapatite As High Performance Catalysts for Low Temperature CO Oxidation

Facile Synthesis of MnO2@SiO2/Carbon Nanocomposite-based Gold Catalysts from Rice Husk for Low-Temperature CO Oxidation

Enhancing the Low-Temperature CO Oxidation over CuO-Based -MnO<sub>2</sub> Nanowire Catalysts

Effect of Pretreatment Atmosphere on CO Oxidation over Α-Mn2o3 Supported Gold Catalysts

Very Low Temperature CO Oxidation over Atomically Precise Au 25 Nanoclusters on MnO 2

Heterostructured Catalysts Prepared by Dispersing Au@Fe2O3 Core–shell Structures on Supports and Their Performance in CO Oxidation

Carbon Monoxide Combustion on Metal Oxide Supported Au@CuxO Catalysts at Low Temperature

Transition Metal (fe2o3, Co3O4 and NiO)-Promoted CuO-Based Α-Mno2 Nanowire Catalysts for Low-Temperature CO Oxidation

High Activity of Gold/Tin-Dioxide Catalysts for Low-Temperature CO Oxidation: Application of a Reducible Metal Oxide to a Catalyst Support

DRIFTS-MS Investigation of Low-Temperature CO Oxidation on Cu-Doped Manganese Oxide Prepared Using Nitrate Aerosol Decomposition

In-situ fabrication of Cu-Mn-O nanostructure catalysts on Ti mesh and their catalytic property optimization for low-temperature and stable CO oxidation

Insights into CO oxidation on Au/TiO2-HMor zeolite catalysts at low temperature

Alumina hollow microspheres supported gold catalysts for low-temperature CO oxidation: effect of the pretreatment atmospheres on the catalytic activity and stability

Design and Synthesis of Rattle-type Au@MnO2 Hollow Nanospheres As Catalysts for CO Oxidation