Abstract:High molecular weight polyether polyols are widely used. However, there is not only a large risk of reaction heat, but also a long reaction time in its traditional production process by using the semi-continuous reactor. The microchannel reactor（MCR） has the characteristics of high heat transfer efficiency and process safety,but the viscous material and high reaction heat release make it difficult to produce the high molecular weight polyether polyols. In this work, using double metal complex（DMC） as catalyst and n-hexane as solvent, the ringopening polymerization of propylene oxide（PO） was carried out in MCR. Polypropylene glycol（PPG） with molecular weight ranging from 2000 to 8000 was prepared. Effects of reaction conditions, such as flow rate, channel length,reaction temperature and feed policy, were investigated. It has been found that when the residence time is long enough, the molecular weight of the produced PPG is basically equal to the theoretical molecular weight. When the flow rate of initiator is fixed, an increase in flow rate of monomer will result in the molecular weight distribution（MWD） first widened and then narrowed. If the tube length is longer, the molecular weight is larger and the MWD is wider. If the temperature increases, the induction period of the polymerization can be shortened. Using the segmented feed, it is easier to prepare high molecular weight PPG with higher conversion than using the single feed, but the MWD is wider. These rules can be explained from the mechanism of PO ring-opening polymerization catalyzed by DMC and micro-mixing strength of materials in MCR. The lower the micro-mixing strength, and the smaller the rate ratio of chain transfer to chain propagation in polymerization, the wider the molecular weight distribution is.

Flow Synthesis of Medium Molecular Weight Polyisobutylene Coinitiated by AlCl3

Preparation of high molecular weight polypropylene glycol in microchannel reactor

Continuous Synthesis of Isobutylaluminoxanes in a Compact and Integrated Approach

Polymerization of 1,3-Butadiene Catalyzed by Ion-Pair Cobalt Complexes with (benzimidazolyl)pyridine Alcohol Ligands

Fast Flow Synthesis of Highly Reactive Polyisobutylene Co-Initiated by an Alcl3/Isopropyl Ether Complex

Cationic Polymerization of Isobutylene Catalysed by AlCl3 with Multiple Nucleophilic Reagents

Generation of Poly(Isobutene-Co-Isoprene) in A Microflow Device

A Complexed Initiating System AlCl3·Phenetole/TiCl4·H2O with Dominant Synergistic Effect for Efficient Synthesis of High Molecular Weight Polyisobutylene.

Facile Synthesis of Medium Molecular Weight Polyisobutylene with Remarkable Efficiency Employing the Complexed BF3·EtOH/TiCl4·H2O Initiating System

Tailoring the AlCl3/iPr2O/Et2O Initiation System for Highly Reactive Polyisobutylene Synthesis in Pure N-Hexane

Cationic polymerization of isobutylene by AlCl3 in n‐hexane and toluene at mild temperatures

Living Cationic Polymerization of Isobutylene in Seconds Based on Microflow System

Synthesis of High Molecular Weight Polyisobutylene Via Cationic Polymerization at Elevated Temperatures

Optimal Flowsheet Configuration of a Polymerization Process with Embedded Molecular Weight Distributions

SYNTHESIS OF HIGHLY REACTIVE POLYISOBUTYLENES WITH BF 3 ·CYCLOHEXANOL INITIATING SYSTEM

Synthesis of Polyethylene with Bimodal Molecular Weight Distribution by Supported Iron‐based Catalyst

Synthesis of branched polyisobutylenes via cationic copolymerization of p ‐chloromethylstyrene and isobutylene

Tunable Synthesis of Propylene Glycol Ether from Methanol and Propylene Oxide under Ambient Pressure

Reverse Atom Transfer Radical Polymerization Of Methyl Acrylate Using Aibn As The Initiator Under Heterogeneous Conditions

Studies on Synthesis of Low Isotactic Polypropylene by Using a Novel MgCl2-supported and Low Ti-loading Catalyst

Micromixing enhanced synthesis of HRPIBs catalyzed by EADC/bis(2-chloroethyl)ether complex