Abstract:Abstract Fabrication of surfaces with hydrophobic and superhydrophobic property has drawn extensive interests as a solution to protect metal surfaces from corrosion attacks, with potential applications in cooling devices for electronics, microfluidic systems for controlled drug delivery, as well as anti-icing, and self-cleaning techniques. This study addresses the impact of surface wettability, i.e., hydrophobicity and superhydrophobicity, on corrosion resistance improvement of metal materials. Hydrophobic and superhydrophobic metal surfaces are desirable to minimize the adhesion between water droplets and the surface. This study aims to fabricate and investigate 17-4 PH stainless steel surfaces with lowered surface energies and modified wetting properties. Various micro- and sub-micro scale finished surfaces with different surface roughness, namely as-received, sandblasted, ground, and polished, were employed, followed by applying a low energy superhydrophobic coating to fabricate hydrophobic and superhydrophobic surfaces on 17-4 PH stainless steel base material. The specific impacts of the surface roughness on wettability and corrosion resistivity of the manufactured surfaces were examined. The ground and polished surfaces followed by applying a 30–50 μm thick superhydrophobic dip coating resulted in steady-state contact angles of up to 152° and 146°, respectively, while the non-engineered coated base metal exhibited the contact angle of 140°. The ground surface with the average surface roughness (Ra) of ∼ 0.03 μm has the optimal roughness. According to the Cassie-Baxter model, the coated ground surface can retain the entrapped air within its interstices more adequately than the other surfaces with either lower surface roughness, such as the polished surface with the roughness of 0.02 μm, or higher surface roughness, such as as-received and sandblasted surfaces with the Ra value of 5.52 μm and 11.98 μm, respectively. To study the corrosion performance and electrochemical stability of the fabricated surfaces, cyclic polarization testing (CPT) and electrochemical impedance spectroscopy (EIS) were performed in an aerated 3.5 wt.% NaCl solution that mimics seawater environment. The electrochemical measurements confirmed that the water-repelling property of the surface contributes to the anti-corrosion capability of the substrate. Data from the corrosion tests indicate that the lowest corrosion current density, highest corrosion potential, and highest pitting potential, were found for the coated ground surface followed by the coated polished surface. The EIS results also highlighted the significantly greater absolute value of impedance for the coated ground and coated polished surfaces even after 240 hrs of immersion in the electrolyte solution than the other fabricated surfaces at lower frequency ranges. The improvement in the 17-4 PH stainless steel corrosion performance was contributed to the size of the fabricated surface micro- and sub-micro scale features, capable of retaining the entrapped air within the roughened surface structure when fully immersed in a corrosive environment. This work demonstrates the effectiveness of a simple fabrication process to create hydrophobic and superhydrophobic stainless steel surfaces with improved corrosion resistivity.

Fabrication of Biomimetic Superhydrophobic Steel Surface under an Oxygen Rich Environment

Fabrication of a Novel Superhydrophobic and Superoleophilic Surface by One-Step Electrodeposition Method for Continuous Oil/water Separation

Preparation of superhydrophobic nanoplate iron oxide surface on a carbon steel for anti-wetting applications

Preparation of super-hydrophobic surface on stainless steel

An easy-to-implement method for fabricating superhydrophobic surfaces inspired by taro leaf

Superhydrophobic LDH/TTOS composite surface based on microstructure for the anti-corrosion, anti-fouling and oil-water separation application

One-Step Fabrication of Robust Superhydrophobic Steel Surfaces with Mechanical Durability, Thermal Stability, and Anti-icing Function.

An Environment-Friendly Fabrication of Superhydrophobic Surfaces on Steel and Magnesium Alloy

Fabrication and Characterization of Durable Superhydrophobic and Superoleophobic Surfaces on Stainless Steel Mesh Substrates

Fabrication of Air-Permeable Superhydrophobic Surfaces with Excellent Non-Wetting Property

Fabrication of superhydrophobic, permeable, and anti-reflective porous steel surfaces using laser ablation and heat treatment

A wear-resistant superhydrophobic surface on Q235 steel prepared by electrospark deposition and electrochemical etching

Fabrication of superhydrophobic surfaces with hierarchical structure and their corrosion resistance and self-cleaning properties

Superhydrophobic surface fabricated by nanosecond laser and perhydropolysilazane

Robust Fabrication of Fluorine-Free Superhydrophobic Steel Mesh for Efficient Oil/water Separation

Constructing Superhydrophobic WO3@TiO2 Nanoflake Surface Beyond Amorphous Alloy Against Electrochemical Corrosion on Iron Steel

A novel method to prepare superhydrophobic, UV resistance and anti-corrosion steel surface

Superhydrophobic surface based on micro/nano structured ZnO nanosheets for high-efficiency anticorrosion

Fabrication and Corrosion Performance of a Superhydrophobic Stainless Steel Surface

Uniting Superhydrophobic, Superoleophobic and Lubricant Infused Slippery Behavior on Copper Oxide Nano-structured Substrates

Fabrication of Superhydrophobic Surface with Different Metal Films on Aluminum Alloy