Ultrafine ZnSe Encapsulated in Nitrogen-Doped Porous Carbon Nanofibers for Superior Na-Ion Batteries with a Long Lifespan and Low-Temperature Performance
Xuewen Wang,Weiming Zhao,Wei Zhang,Ka Wai Wong,Jiawei Wu,Tong Chen,Shaoming Huang
DOI: https://doi.org/10.1021/acssuschemeng.1c02447
2021-08-25
Abstract:The inferior cycle lifespan and unsatisfactory energy density of traditional anode materials for sodium-ion batteries need to be improved toward actual application. Here, MOF-derived ultrafine ZnSe nanoparticles encapsulated within nitrogen-doped porous carbon nanofiber composites () are fabricated via in situ pyrolysis and selenylation from electrospun nanofibers. As an anode, the electrode displays outstanding sodium-storage performance and superior cycling stability (197.3 mAh g–1 after 1700 cycles at 10 A g–1). Remarkably, the assembled SIBs work well in low temperatures within the range from −20 to −40 °C, showing the prospect for energy storage in an extreme environment. The impressive electrochemical properties are primarily due to the peculiar porous framework and ultrafine ZnSe nanoparticles, as well as a robust N-doped carbon matrix, which provide a penetrating network for fast ion/electron transfer and alleviate the pulverization of ZnSe during a sodiation/desodiation reaction. Moreover, the underlying reaction mechanism and outstanding reversibility of the electrodes are systematically revealed through ex situ X-ray diffraction/scanning electron microscopy (XRD/SEM) analysis and dynamic analysis.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.1c02447.Experimental details; calculation process of the diffusion coefficient and the capacitance effect; FESEM images of ZIF-8, nanofibers, and pure PAN nanofibers; TEM images of nanofibers (Figure S1); FESEM, TEM, HRTEM, and EDS mapping images of (Figure S2); XRD patterns of ZIF-8 and (Figure S3); FESEM images of NC and NCNF (Figure S4); XRD pattern of NC and NCNFs (Figure S5); TG curves and the calculation process of the C content in and (Figure S6); BET curve of the composite (Figure S7a); pore size distribution image of the composite (Figure S8) and the composite (Figure S7b); CV and charge-–discharge curves of the electrode (Figure S9); FESEM images and EDS mapping images of after 200 cycles (Figure S10); EIS curves of and (Figure S11); rate and cycling tests of the NC and NCNFs (Figure S12); ex situ FESEM images of (Figure S13); fitted resistance values of EIS results (Table S1); and comparison of sodium-storage performance (Table S2) (PDF)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology