Large transport J c in Cu-sheathed Sr 0.6 K 0.4 Fe 2 As 2 superconducting tape conductors

He Lin,Chao Yao,Haitao Zhang,Xianping Zhang,Qianjun Zhang,Chiheng Dong,Dongliang Wang,Yanwei Ma
DOI: https://doi.org/10.1038/srep11506
IF: 4.6
2015-01-01
Scientific Reports
Abstract:Copper sheath is the first choice for manufacturing high- T c superconducting wires and tapes because of its high electrical and thermal conductivities, low-cost and good mechanical properties. However, Cu can easily react with superconducting cores, such as BSCCO, MgB 2 and pnictides and therefore drastically decrease the transport J c . Here, we report the fabrication of Cu-sheathed Sr 1−x K x Fe 2 As 2 tapes with superior J c performance using a simple hot pressing method that is capable of eliminating the lengthy high-temperature sintering. We obtained high-quality Sr 1−x K x Fe 2 As 2 tapes with processing at 800 o C for 30 minutes and measured high T c and sharp transition. By this rapid fabrication, Cu sheath does not give rise to apparent reaction layer and only slightly diffuses into Sr-122 core. As a consequence, we achieved high transport J c of 3.1 × 10 4 A/cm 2 in 10 T and 2.7 × 10 4 A/cm 2 in 14 T at 4.2 K. The in-field J c performance is by far the highest reported for Cu-sheathed high- T c conductors. More importantly, Cu-sheathed Sr-122 tapes also showed a high J e value of 1.0 × 10 4 A/cm 2 in 10 T at 4.2 K, which has reached the widely accepted practical level for applications. These results demonstrate that Cu is a very promising sheath for the practical application of pnictide conductors.
What problem does this paper attempt to address?