Tunable Single‐Phase White Light Emission from Complex Perovskite Sr3CaNb2O9: Dy3+/Eu3+ Phosphors
Noor Zamin Khan,Sayed Ali Khan,Nisar Muhammad,Weilong Chen,Jahangeer Ahmed,Muhammad Amin Padhiar,Mei Chen,Marcin Runowski,Saad M. Alshehri,Baohua Zhang,Shu‐Sheng Pan,Ren‐Kui Zheng
DOI: https://doi.org/10.1002/adom.202401938
IF: 9
2024-12-08
Advanced Optical Materials
Abstract:This article presents the Sr3CaNb2O9:Dy3+/Eu3+ samples using a high‐temperature solid‐state reaction method. Photoluminescence spectroscopy measurements demonstrate that incorporating Dy3+ and Eu3+ ions enabled adjustable luminescent performance at a targeted excitation wavelength, leading to emission in multiple colors. Varying the concentration of Eu3+ allowed for shifting luminescent colors from yellow to orange red, achieving warm white light emission. Sr3CaNb2O9:Dy3+/Eu3+ phosphors with a complex perovskite structure are prepared using a high‐temperature solid‐ state reaction technique. These phosphors are doped either singly or in combination with Dy3+/Eu3+ ions, resulting in efficient energy transfer from Dy3+ to Eu3+ and thus tunable‐color emission. Under 353 nm excitation, the Sr3CaNb2O9:Dy3+ phosphor emits blue (492 nm), yellow (583 nm), and red (682 nm) light, with the optimal doping concentration of Dy3+ of 0.04%. When excited by 394 nm (7F0 → 5L6), the Sr3CaNb2O9:Eu3+ phosphor exhibits two most intense emissions centered at 593 nm (5D0 → 7F1) and 614 nm (5D0 → 7F2). The decrease in luminescence intensity with increasing doping concentration of Dy3+ and Eu3+ is due to the cross‐relaxation associated with electric dipole–dipole interaction. Photoluminescence emission measurements under excitations of 353 and 365 nm indicate that the Sr3CaNb2O9:0.04Dy3+/0.05Eu3+ phosphor shows excellent thermal stability, even at a temperature of 150 °C, where the luminescence intensity preserves 79% of its initial value at room temperature. The electroluminescence performance of the Sr3CaNb2O9:0.04Dy3+/0.05Eu3+ phosphor is tested with 365 nm LED chips for potential use in white LEDs. The results confirm that Sr3CaNb2O9:0.04Dy3+/0.05Eu3+ phosphor has great potential for use in high‐power white LED applications as a single matrix.
materials science, multidisciplinary,optics