A Scalable Approach for Dendrite-Free Alkali Metal Anodes Via Room-Temperature Facile Surface Fluorination.

Gang Wang,Xunhui Xiong,Dong Xie,Xiangxiang Fu,Zhihua Lin,Chenghao Yang,Kaili Zhang,Meilin Liu
DOI: https://doi.org/10.1021/acsami.8b18101
IF: 9.5
2019-01-01
ACS Applied Materials & Interfaces
Abstract:Alkali metals are attractive anode materials for advanced high-energy density battery systems because of their high theoretical specific capacities as well as low electrochemical potential. However, severe dendrite growth as well as high chemical reactivity restrict their practical application in energy storage technologies. Herein, we propose a facile scalable solution-based approach to stabilize Li and Na anodes via the facile process of immersing the Li/Na metal in a nonhazardous ionic liquid 1-butyl-2,3-dimethylimidazolium tetrafluoroborate for several minutes at room temperature before battery assembly. This produces a dense and robust artificial fluoride layer, formed in situ by the reaction of the ionic liquid and Li/Na metal. As a demonstration, a homogeneous and compact LiF coating on the Li metal anode was fabricated via our method and it can effectively suppress the growth of Li dendrites and the continuous decomposition of electrolytes during cycling. As a result, the LiF-coated metallic Li anode achieves an enhanced cycling lifespan of over 700 h with low overpotential (similar to 22 mV) at 1 mA cm(-2), as well as a very high Coulombic efficiency of up to 98.1% for 200 cycles at 1 mA cm(-2). Furthermore, the successful achievements of the dendrite-free Na deposition show the versatility of room-temperature surface fluorination for potential battery applications.
What problem does this paper attempt to address?