n-Butyltin(IV) trichloride initiator for the solvent-free ring-opening polymerization of ε-caprolactone: evaluation of the structure-reactivity relationship of tin(IV) derivatives
Wanich Limwanich,Boontharika Thapsukhon,Puttinan Meepowpan,Watcharee Funfuenha,Manita Dumklang,Samuch Taweekasemsombat,Winita Punyodom
DOI: https://doi.org/10.1007/s00289-024-05310-0
IF: 2.843
2024-08-24
Polymer Bulletin
Abstract:The n -butyltin(IV) trichloride ( n BuSnCl 3 ) initiator was successfully utilized in the ring-opening polymerization (ROP) of ε -caprolactone ( ε -CL) under solvent-free conditions. Its reactivity was investigated by the non-isothermal differential scanning calorimetry (DSC). Effect of n BuSnCl 3 concentration on the ROP of ε -CL was investigated by the Kissinger and model fitting methods. The obtained activation energy ( E a ) values for the ROP of ε -CL with 1.0 mol% of n BuSnCl 3 were higher than 2.0, and 4.0 mol%, respectively. Furthermore, the degree of aggregation ( m ) of n BuSnCl 3 in the ROP of ε -CL was determined by the DSC technique. From the obtained m values at 120 and 140 °C, n BuSnCl 3 presented in a non-aggregated state in the non-isothermal ROP of ε -CL. The performance of n BuSnCl 3 was also compared with the di- n -butyltin(IV) dichloride ( n Bu 2 SnCl 2 ) and tri- n -butytlin(IV) chloride ( n Bu 3 SnCl). The number of chloride and n -butyl groups adjacent to the Sn active center significantly affected the solvent-free ROP of ε -CL. From the non-isothermal DSC measurement, the polymerization exotherms for the ROP of ε -CL with n BuSnCl 3 occurred and were completed at a lower temperature range than n Bu 2 SnCl 2 , and n Bu 3 SnCl, respectively. The E a value for the ROP of ε -CL initiated by n Bu 3 SnCl was higher than n Bu 2 SnCl 2, and n BuSnCl 3 , respectively. The values of pre-exponential factor (ln A ) for the ROP of ε -CL initiated by n Bu 3 SnCl, n Bu 2 SnCl 2, and n BuSnCl 3 were determined from the first order reaction model fitting ( f ( α ) = 1− α ) and compensation effect. The kinetics data demonstrated that the reactivity of n BuSnCl 3 was higher than n Bu 2 SnCl 2, and n Bu 3 SnCl due to the lowest steric hindrance and the highest Lewis acidity of n BuSnCl 3 . Larger-scale (250 g) polymerization of ε -CL was preliminarily investigated by using the highly reactive n BuSnCl 3 initiator. n BuSnCl 3 could effectively produce PCL with weight average molecular weight ( M w ) of 7.1 × 10 4 g/mol and 82% yield at 150 °C for 24 h. The probable mechanism of the ROP of ε -CL with n Bu 3 SnCl was proposed via the coordination-insertion mechanism.
polymer science