Hot Hydroforming of 22mnb5 Tube by Resistance Heating

G. N. Chu,Y. L. Lin,M. Q. Ding

DOI: https://doi.org/10.1007/s11837-016-1938-6

2016-01-01

JOM

Abstract:To promote the application of high strength steels in automobile bodies, the practicability of hot hydroforming of tube by resistance heating is illustrated. From the results of experiments conducted to measure temperature distributions of the tube during the forming process, a method to improve temperature uniformity has been proposed and achieved. Validity was evaluated by examining the effects of hot gas forming on the microstructure and hardness. Results indicate an obvious temperature difference along the axial direction for two cross-sectional shapes: the temperature in the middle zone of the tube is higher than that at its ends. Both thermal convection and cross-sectional shape have only a limited effect on the temperature distribution. The main reason for non-uniform temperature distribution is the heat transition between the electrodes and the tube ends. The temperature difference decreased as the heating rate increased. In contrast, the temperature distribution was even along the circumferential direction for both cross-sectional shapes. Adjusting the contact resistance is a useful method of reducing the temperature difference. In this study, the temperature difference was successfully decreased to 20°C, while reaching a maximum temperature of 750°C, which is adequate for both forming and quenching. A rectangular component was formed to validate the practicality and efficiency of tube hot hydroforming by resistance heating. The hardness and microstructure met the requirements of 22MnB5, which demonstrates both the forming efficiency and quantity advantages of hot gas hydroforming by resistance heating.